  • Ultrasonic Velocity in Binary Solution of Polyethylene Oxide With Water
  • Shin WG, Moon TJ, Bae JL, Paik WS
  • Polyethylene oxide/물의 이성분용액에서의 음속
  • 신원규, 문탁진, 배종림, 백운석
Abstract
In this stu요 the sonic velotities of four po1yethylene oxide(PO)/water binary solutions were measured weight of PO, by the method of multireflection of ultrasonic pulses in a few MHz frequency ranges. The sonic velocities and viscosities of the solutons were measured at the temperature ranges of 25℃∼60℃ and at the concentration ranges of 1 wt%∼3 wt% by a pulseecho-overlap method and by an Oswald viscometer, respectively. It is found that the sonic velocities of the solutions increase as the temperatures and the concentrations increase in general

본 실험에서는 분자량이 다른 4개의 polyethylene oxide(PO)물 2성분용액의 음속을 초음파 pulse의 다중반사에 의한 수 MHz의 주파수영역에서 측정하였다. PO/물 2성분용액의 음속과 점성도를 각각 pulse-Echo-Overlap방법과 Oswald점도계를 사용하여 25℃∼60℃의 온도구간과, 1wt%∼3wt%의 농도구간에서 온도와 농도를 각각 변화시키면서 대기압하에서 측정하였다. 용액의 음속은 온도와 농도가 증가함에 따라 증가함을 알 수 있었는데 이는 일반적으로 농도증가에 따른 compressibility의 감소 때문인 것으로 생각된다. 온도와 농도에 따를 점성도는 일반적인 결과를 나타냄을 알수 있었으며, PO의 분자량에 따른 음속의 변화는 분명하게 알 수 있었다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1993; 17(6): 637-643

    Published online Nov 25, 1993

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: