  • Performance Improvement of Unsaturated Polyester/Alumina Composites for Organic Building Material : (I) Surface Treatment of Filler
  • Choe CR, Jang JS
  • 유기 건축 복합재용 불포화 폴리에스테르/알루미나 복합재료의 물성향상: (Ⅰ) 충전재의 표면처리에 따른 고찰
  • 최철림, 장정식
Abstract
In order to apply for organic building material, unsaturated polyester/alumina composites have been fabricated using orthophthalic unsaturated polyester matrix resin. Alumina, as a filler, was surface treated with variation of silane concentration and the modified alumina surface was analyzed by FT-IR-DRIFT method. Compared with untreated alumina/unsaturated polyester composite, surface treated alumina/unsaturated polyester composites have retained the increased mechanical properties and optimum silane Concentration, which shows the maximum mechanical properties of unsaturated polyester/alumina composite. exists irrespective of the type of silane coupling agent. In addition, the relationship between silane concentration and the mechanical properties of unsaturated polyester/alumina composites was also discussed.

유기건축 복합재료의 대표적인 수지인 orthophthalic게 불포화 폴리에스테르를 매트릭스 수지로 사용하여 불포화 폴리에스테르/알루미나 복합재료를 제조하였다. 충전재인 알루미나의 표면을 실란 카플링제의 농도 변화에 따라 처리하여 충전재/매트릭스 수지의 계면 개질화를 시도하였으며, FT-IR DRIFT 방법에 의해 알루미나 표면을 분석하였다. 실란 카플링제로 알루미나 표면을 처리시 미처리 알루미나의 경우에 비해 불포화 폴리에스테르/알루미나 복합재료의 기계적 물성이 증가하였으며, 실란 카플링제의 종류에 관계없이 기계적 물성의 최대치를 나타내는 최적 실란농도가 존재하였다. 또한 실란 카플링제의 농도와 복합재료의 기계적 물성에 대한 상관관계도 고찰하였다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1993; 17(6): 703-709

    Published online Nov 25, 1993

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: