Polytitanomethylsilanes (PTMS) were synthesized by the reaction of titanium tetrabutoxide (Ti(OC₄H₉)₄) and polymethylsilane (PMS) which showed low ceramic yield but contained highly reactive Si-H bonds. Then PTMS, ceramic precursors, were characterized by R, NMR, GPC and TGA, resulting in much improved ceramic yield up to 83%. Precerarmic PTMS were converted to cerarmic composites of carbides and oxides when heated over 1300℃ under inert atmosphere. That is, SiC/TiC/SiO₂ ceramic mixture was obtained for 6 mole% of Ti(OC₄H₉)₄/PMS, and four-components ceramics containing TiO₂ for 15 mole%, and β-SiC/TiC/SiO₂/Ti₃O₅/α-SiC was Produced for 33 mole% .

열분해 수율은 매우 낮으나 반응성이 강한 Si-H을 많이 포함한 polymethylsilane (PMS)과 titanium tetrabutoxide (Ti(OBu)₄)를 반응시켜 polytitanomethylsilanes (PTMS)을 합성한 뒤 IR, NMR, GPC, TGA를 사용하여 세라믹 전구체로서의 물성을 분석하였다. 세라믹 수율이 최고 83%까지 개선된 PTMS는 불활성 분위기와 1300℃ 이상에서 열분해하여 carbide와 oxide를 포함한 복합 세라믹으로 전이되었다. 세라믹 조성은 Ti(OC₄H₉)₄/PMS의 반응 몰비가 6%일때는 SiC /TiC/SiO₂의 3성분 세라믹스가 얻어졌고 15%인 경우 TiO₂를 형성하여 4성분 세라믹스를, 그리고 반응 몰비가 33%일 때는 Ti의 상대적 함량이 큰 Ti₃O₅이 형성되어 β-SiC/TiC/SiOM₂/Ti₃O₅/α-Sic 5성분 세라믹스가 얻어졌다.

Keywords: