Two fiber fragmentation technique was used to investigate the influence of hydrothermal on the interfacial shear strength in the carbon fiber/epoxy system. The uptake of water (wt%) and interfacial shear strength were evaluated up to 60 days of immersion time in distilled water at 75℃ using two fiber fragmentation test specimens of dogbone shape. As a result, it was found that moisture absorption of two fiber doggone specimens increased with time of exposure to hydrothermal. This induced to increase the average critical aspect ratio (L_c/D_f) of the fiber fragments. The increase of L_c/D_f for hydrothermally treated samples indicated the decrease of the interfacial shear strength by increasing of moisture absorption.

탄소섬유/에폭시 복합재료에서 계면전단강도의 수분에 대한 내구성을 조사하기 위해 두섬유 fragmentation 시험법을 사용하였다. Dogbone형의 두섬유 fragmentation 시험편을 제작하여 75℃의 증류수에 60일까지 침지시켜 수분 흡수량을 측정하였으며, 수분 흡수량에 따른 계면특성 및 계면전단강도를 평가하였다. 그 결과, 침지시간의 경과에 따라 시험편에 흡수된 수분량은 증가하였고, 이러한 수분 흡수량의 증가는 섬유와 수지의 계면을 열화시켜 파단된 섬유길이의 임계 aspect ratio (임계섬유장/섬유직경)를 증가시켰으며, 이것은 곧 수분흡수량의 증가에 의해 복합재료에서 계면전단강도의 감소를 나타내는 것이다.

Keywords: hydrothermal; fragmentation test; interfacial shear strength; durability; degradation