  • A Study on the Synthesis of ACF/PP-g-AN Hybrid Fibers by Irradiation and Separation of Uranium
  • Hwang TS, Hwang DS, Nho YC
  • 방사선 중합에 의한 ACF/PP-g-AN 복합섬유의 합성 및 우라늄 분리에 관한 연구
  • 황택성, 황대성, 노영창
Abstract
The ACF/PP-g-AN copolymers were synthesized by the irradiational grafting of acrylonitrile onto ACF/PP hydrid fabric. The synthesis of the ACF/PP-g-AN copolymer was evidenced by the band of -C≡N absorption peak at 2250cm-1 and amidoximation was evidenced by the band of -OH and -NH2peak at 3450cm-1 on FT_IR spectrum. The optimal time for the uranium ion adsorption equilibrium on ACF/PP-g-AN copolymers was 8 days and the optimal pH was 8. The adsorption capacities of ACF/PP-g-AN copolymers increased according to the content of amidoxime and were not varied even after more than 10 times of regeneration.

방사선 전조사법을 이용하여 아크릴로니트릴을 ACF/PP 복합섬유에 그라프트 반응시켜 섬유형 ACF/PP-g-AN 공중합체를 합성하였다. 합성한 공중합체의 FT-IR 결과 2250cm-1 부근에서 -C≡N에 대한 피크, 3450cm-1 부근에서 -OH와 -NH2에 의한 피크 확인으로 그라프트 반응 및 아미드옥심화 반응을 확인할 수 있었다. 아미드옥심화된 ACF/PP-g-AN 공중합체의 우라늄 이온에 대한 흡착능의 최적시간은 8일이었으며, 최적 pH는 8이었다. 동일 조건하에서의 흡착능은 아미드옥심기으이 함량이 증가할수록, 그라프트율이 116.3%일 때 최대 흡착능을 나타내었다. 또한 ACF/PP-g-AN 공중합체는 10회 이상 흡착능으이 면화없이 흡탈착이 가능한 흡착제임을 알 수 있었다.

Keywords:

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2000; 24(2): 174-181

    Published online Mar 25, 2000

  • 10.7317/pk.
  • Received on Nov 30, -0001
  • Revised on Nov 30, -0001
  • Accepted on Nov 30, -0001

Correspondence to

  • E-mail: