The positive temperature coefficient (PTC) effects of high density polyethylene (HDPE)/carbon black composite materials were investigated by enhancing adhesive characteristics of electrodes and controlling HDPE chemical crosslinking. When the silver paste was used as an electrode for the same 45 wt% HDPE/carbon composites, the resistance was over 1 Ω, which should be compared with the resistance of 0.2 Ω for the dendritic copper electrode. In general, the silver-paste electrode exhibited higher electrical resistance than cupper electrode due to the interfacial resistance between the electrode and PTC composites. The HDPE/carbon composite exhibited typical PTC characteristics maintaining a constant resistance up to vicat point and showing a maximum at the melting point of HDPE. The crosslinked HDPE significantly decreased the negative temperature coefficient (NTC) phenomena, and desirably showed a constant or slightly increasing feature of electrical resistance in the high temperature region.

접착성이 없는 고밀도 폴리에틸렌 (HDPE)과 나노입자 카본블랙 복합체를 대상으로 전극과의 계면 접착 향상과 고분자 가교 특성에 따른 양온도 계수 (PTC) 특성을 연구하였다. 은페이스트를 전극으로 사용하였을 때에는, 전극과 HDPE의 접착 계면 저항으로 인하여 카본함량이 45 wt% 이상에서 1 Ω 이었으나, 덴드라이트(dendrite)된 구리 전극의 경우 HDPE와 전극간의 넓은 면적 접촉에 의한 계면 저항이 0.2 Ω이하였다. HDPE와 은페이스트의 계면 저항의 증가로 인하여 구리 박막을 사용하였을 때보다 전체적으로 저항이 높게 나타났다. HDPE와 나노입자 카본블랙 복합체는 온도가 증가하여 HDPE의 비캣연화온도까지는 저항이 일정하게 유지하다가, HDPE의 연화점에서 증가하기 시작하여 용융점에서 극대 값을 나타내는 전형적인 PTC특성을 보여주었다. 일반적으로 HDPE의 용융점을 넘어서면 음온도 계수 (NTC) 현상이 나타나는데, 가교 결합을 시킨 HDPE의 경우는, 용융점 이상에서 NTC 현상이 나타나지 않고 저항이 일정하게 유지되거나 증가하는 경향이 나타났다. 구리 (copper) 전극과 고분자와의 계면 접촉 면적을 증가시키기 위하여 크롬 (chromium)을 덴드라이트시킨 전극을 사용하여 계면 접촉 저항을 감소시켰다.

Keywords: positive temperature coefficient (PTC); negative temperature coefficient (NTC); interfacial adhesion; crosslinking; dendrite