  • Study on the Pressure-Volume-Temperature Properties of Polypropylene at Various Cooling and Shear Rates
  • Pengcheng Xie*, Huaguang Yang*, Tianze Cai*, Zheng Li*, Yuelin Li*, and Weimin Yang*,**,†

  • *College of Mechanical and Electrical Engineering, Beijing University of Chemical Technology, Beijing, PRC
    **State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, PRC

  • 다양한 냉각속도와 변형률속도에서 폴리프로필렌의 압력-부피-온도 특성에 관한 연구
Abstract

To understand the pressure-volume-temperature (PVT) properties of polymer in injection process, a dilatometer with high cooling rate (up to 25 ℃/s) and shear rate (up to 320 s-1) was developed. The working pressure and temperature of the dilatometer range from 0 to 100 MPa, and from 30 to 300 ℃, respectively. With this instrument, a crystalline polymer polypropylene (PP) was employed to study the effects of cooling rate, shear rate, pressure and their coupling effect on its PVT properties. It was demonstrated that the cooling rate showed a significant effect on the PVT properties. With the increase of cooling rate, the transition temperature of PP from melt state to crystallization decreases gradually and the temperature range of crystallization was also extended. Shear increased the transition temperature of PP from melt state to crystallization. Meanwhile, the initial temperature of shear and crystalline segment was shifted to a higher temperature region with increasing shear duration or shear rate. Above the transition temperature, the effect of shear on the PVT properties weakened gradually with increasing the initial temperature. The coupling analysis of cooling and shear processes showed that increase in cooling rate was enhanced the effect of shear on the transition temperature of PP from melt state to crystallization.


Keywords: pressure-volume-temperature properties, cooling rate, shear rate, crystallization.

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2018; 42(2): 167-174

    Published online Mar 25, 2018

  • 10.7317/pk.2018.42.2.167
  • Received on Mar 22, 2017
  • Revised on Jul 11, 2017
  • Accepted on Oct 1, 2017

Correspondence to

  • Weimin Yang
  • *College of Mechanical and Electrical Engineering, Beijing University of Chemical Technology, Beijing, PRC
    **State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing, PRC

  • E-mail: yangwm@mail.buct.edu.cn