  • Relationship between Weather-Resistance and Mixing Ratio of Mill-Base and Let-Down Silicone/Acrylic Resins
  • Jo HJ, Shim IW, Hahm HS, Park HS
  • 안료분산용 및 희석용 실리콘/아크릴수지의 배합비와 내후성과의 상관관계
  • 조혜진, 심일우, 함현식, 박홍수
Abstract
In order to investigate the effect of the composition of weather-resistant coatings on physical properties, three different weather-resistant coatings were prepared by varying the ratio of a mill-base silicone/acrylic resin and let-down silicone/acrylic resin in weight ratios of 2:8, 3:7, and 4:6. The physical properties and weather-resistance of the prepared coatings were tested. It was found that the thermal stability, salt spray exposure, and weather-resistance were improved with increasing the amount of silicone. The optimum mixing ratio of mill-base silicone/acrylic resin to the let-down silicone/acrylic resin was 2:8. The coating containing silicone component of 30 wt% was found to be suitable as high weather-resistant coatings.

실리콘/아크릴수지를 기반으로 한 내후성 도료의 조성이 물성에 미치는 영향을 연구하기 위하여 안료분산용 및 희석용 실리콘/아크릴수지의 배합비를 중량비율 2:8, 3:7, 4:6의 3종으로 변화시키면서 내후성 도료를 제조하였다. 제조된 도료의 도막물성 및 내후성이 판단할 수 있는 각종 도막실험을 실시한 결과, 실리콘 성분함량이 증가할수록 열적안정성, 염수분무 및 내후성 등이 향상되었으며, 적정배합비는 2:8임을 알 수 있었다. 또한 실리콘 성분을 30 wt% 함유한 도료는 고내후성을 보유함을 확인하였다.

Keywords: -base; let-down; silicone/acrylic resin; weather-resistant coatings

  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2006; 30(4): 350-356

    Published online Jul 25, 2006

  • 10.7317/pk.
  • Received on Feb 2, 2006
  • Revised on Nov 30, -0001
  • Accepted on Jul 3, 2006

Correspondence to

  • E-mail: