Polyurethanes (PUs) containing poly(dimethyl siloxane) (PDMS) unit in soft segment, PU-Si, were synthesized, and their mechanical properties and phase separation were investigated. Various amounts of PDMS units were incorporated into PU via a solution polymerization method in N,N'-dimethylformamide using poly(tetramethylene ether glycol) and PDMS diol as a soft segment and methylene diphenyl diisocyanate and 1,4-butanediol as a hard segment. Two series of PU-Si samples with an HS content of 23% and 32% were prepared and analyzed. Results showed that the elongation-at-break of the PU-Si films increased, breaking stress decreased, and the hydrophobicity of the film increased as the PDMS content in PU-Si increased. SAXS analysis indicated that the microphase separation of the PU-Si film between hard and soft segments decreased with increasing PDMS content, irrespective of the HS content.

메틸렌디페닐 디이소시아네이트와 1,4-부탄디올을 하드세그먼트(HS) 성분으로 하고, 폴리(디메틸 실록산) (PDMS) 디올과 폴리(테트라메틸렌 에테르 글리콜) (PTMEG) 혼합 폴리올을 소프트세그먼트(SS) 성분으로 하여, HS 함량이 각각 23와 32%이면서 PDMS 성분 비율이 다른 여러가지 PU-Si를 용액중합법으로 합성하고 이들을 필름으로 제조하여 물성과 상분리 구조를 분석하였다. PU-Si 필름에서 PDMS 성분 비율이 커지면 파단응력은 감소하는 반면 파단신도는 증가하였다. PU-Si에 PDMS 성분이 증가할수록 소수성이 커지고 HS와 SS 사이의 상분리는 감소하였다. HS 함량이 32%인 시료들이 HS 함량이 23%인 시료보다 상분리가 잘 되어 있으며, 두 경우 모두 PDMS 성분이 증가하면 상분리 정도가 감소하였다.

Keywords: polyurethane; poly(dimethyl siloxane); mechanical properties; phase separation; SAXS