The stearyl alcohol was encapsulated with waterborne polyurethane (WPU) to prepare a shape-stabilized phase change materials (PCMs) containing stearyl alcohol up to 50 wt%. The particle size analysis and the morphology observed by scanning electron microscope showed that the encapsulated particle size was several micrometers. Thermogravimetric analysis demonstrated that the stearyl alcohol was effectively encapsulated by WPU with marginal loss. The heat of fusion of the particle encapsulating 30 wt% stearyl alcohol was 90-100 J/g, which was larger compared with those of previous reports on PCMs encapsulated by polyurethanes. The shape-stability of stearyl alcohol above melting temperature was evidently improved by the encapsulation with WPU.

형태 안정성를 갖는 상전이 물질을 제조하기 위하여 결정화 및 용융에 따른 잠열이 큰 스테아릴알코올을 수 분산폴리우레탄에 최대 50 wt% 담지한 입자를 물속에서 제조하였다. 냉동건조된 담지 입자가 수 μm 크기를 가지는 것을 입도분석, 그리고 주사전자현미경으로 관찰하였다. 열중량분석 결과, 투입된 스테아릴알코올 손실이 거의 없이 효과적으로 수분산폴리우레탄에 담지되었다. 열적 성질들을 시차주사열량계로 분석한 결과, 스테아릴알코올을 30 wt% 담지한 경우 용융열이 90-100 J/g 수준으로, 이전에 보고된 저분자 상전이물질을 담지한 폴리우레탄들의 다 른 결과들에 비해 높은 값들을 가졌다. 또한 스테아릴알코올의 녹는점 이상에서의 형태 안정성은 수분산폴리우레탄 에 담지됨으로써 크게 향상되었다.

Keywords: stearyl alcohol; waterborne polyurethane; encapsulate; phase change material; shape-stabilized