Maleic anhydride grafted polypropylene (PP-g-MA) with cellulose fiber was studied to improve the adhesion strength in the interface of polypropylene/nylon (PP/N6) multilayer films. It was found that the adhesion strength between PP films and nylon films increased due to the interaction between MA in PP and amide in N6. Further improvement in adhesion strength was achieved by adding nano cellulose fiber with PP-g-MA. Master chips made by PP-g-MA with nano cellulose fiber were mixed with PP and found out that mixing characteristic of nano cellulose fiber in PP was enhanced due to relatively low melt viscosity of PP-g-MA, as a result, the lowering of optical transmittance in PP film by nano cellulose fiber was minimized. The physical interaction between the MA in PP-g-MA and hydroxyl in nano cellulose fiber surface resulted in the increase of Young’s modulus and tensile strength in PP films

폴리프로필렌/나일론 다층 필름의 계면 접착력 향상을 위하여 무수산기가 도입된 폴리프로필렌에 나노 셀룰로오스 섬유를 첨가하여 제조된 필름의 물성 변화를 살펴보았다. 폴리프로필렌의 무수산기와 나일론 필름의 아마이드기 상호 친화성에 따라 폴리프로필렌/나일론 다층 필름 계면 접착 특성이 우수해지며 나노 셀룰로오스 첨가에 의하여 접착 특성이 더 향상됨을 알 수 있었다. 나노 셀룰로오스 섬유를 상대적으로 점도가 낮은 무수산기가 도입된 폴리프로필렌에 혼합하여 마스터 수지를 제조하여 이를 폴리프로필렌에 용융 혼합하는 경우, 나노 셀룰로오스 섬유와 폴리프로필렌의 혼화성이 우수해져 셀룰로오스 섬유 첨가에 따른 폴리프로필렌 필름 광학 특성 감소를 최소화할 수 있었다. 아울러 폴리프로필렌의 무수산기와 셀룰로오스 섬유의 하이드록실기 결합에 의하여 폴리프로필렌 필름의 탄성계수 및 인장강도가 증가됨을 확인하였다

Keywords: nano cellulose fiber, PP/N6 multilayer film, mixing characteristics, peel strength