Fourpolyimides were prepared by the thermal reaction of dianhydride and diamine. Each polymer was compared with their copolymers including oligosiloxane of 1 mol% and 2 mol%. Aminopropyl-ended oligosiloxane, as a diamine comonomer was used in copolymerization and analyzed by ¹H NMR. The presence of oligosiloxane resulted in insignificant change of properties, such as thermal resistance, Young’s modulus and elongation except thermal expansion. Thermal expansion coefficients of the four polyimides reduced as including oligosiloxane. An electric film heater was fabricated to measure thermal resistance of the prepared polymers. The device of 1 mol% siloxane-polyimide showed constant performance at 300 ℃ for 5 h and reproduced in 5 operation cycles. The device of 0 mol% siloxane-polyimide was instable over 250 ℃.

단분자의 종류에 따른 4 종의 폴리이미드를 합성하고 아민 말단의 올리고실록산을 공중합체로 사용하여 내열성 폴리이미드를 제조하였다. 1 mol%와 2 mol%의 실록산이 결합된 공중합 고분자는 ¹H NMR을 통해 구조분석을 하였다. 400 ℃ 전후의 높은 열안정성과 높은 영율 및 연신율 특성은 실록산 존재에 의해 큰 변화를 보이지 않으나 열팽창율 감소가 명확히 관찰되었다. 열특성 평가를 위해 합성된 고분자를 Al-박막에 도포하여 라미네이트형 전열 박막소자 제작을 하였다. 실록산이 없는 경우 250 ℃ 이상에서 온도 불안정성이 나타났으나, 1%의 실록산이 도입된 공중합체의 사용으로 300 ℃의 높은 온도가 구현되었다. 고온에서 약 5시간 동안 안정된 특성을 보였으며 5회 이상의 온도변화 사이클에서 높은 재현성을 보였다.

Keywords: heating resistance, polyimide, siloxane-copolymer, electric heating device, thermal expansion coefficient.