The mechanical properties of epoxy systems modified with a prereacted carboxyl-terminated rubber were investigated in relation to variations in incorporated rubber concentration of up to 20 parts per hundred resins(phr) at a fixed cure condition. Modified epoxy systems cured by 4,4''-diaminodiphenyl sulfone(DDS) were estimated by using scanning electron micrographs (SEM), Instron, optical micrographs, and dynamic mechanical analyser(DMA). The mechanical properties of the modified epoxy systems depend on incorporated rubber content : around 10phr of rubber the systems show maximum tensile fracture energy and the domain size of rubber particles dispersed in epoxy matrix ranges from 0.25㎛ to 5㎛.

고성능 에폭시 수지의 한 종류인 Tetraglycidyl-4,4''-diaminodiphenylmethane (TGDDM)를 carboxyl-terminated 반응성 액상고무로 변성하여 고무함량 변화에 따른 기계적 성질의 변화를 연구하였다. 경화제로는 4,4''-diaminodiphenyl sulfone(DDS)를 사용하였으며, 물성의 측정은 주사현미경, Instron, 광학현미경, Dynamic mechanical analyser(DMA)를 사용하였다. 에폭시 수지의 인장 파괴에너지는 고무함량 10phr 부근에서 최대값을 나타내었으며, 이때 고무입자의 크기는 0.25㎛-5㎛ 정도로 분포하고 있다.