Chitogan was prepared from chitin which was abstracted from the bone of Cuttlefish. Chitosan was then graft-copolymerized with acrylic acid monomer using an initiator, ceric ammonium nitrate(CAN). The grafted-copolymer was identified by using IR spectroscopy and electronic micrographs. The reaction conditions and results were as follows : The percentage of grafting of acrylic acid was increased with increasing CAN concentration up to 3.33×10^-3) M under constant concentration of acrylic acid in 150 ml of 15wt.%-acetic acid solution dissolving 2g chitosan. The weight percentage and viscosity average molecular weights were increased linearly with increasing acrylic acid was also increased with increasing reaction temperature and it showed linearity. With reaction time regardless of the reaction temperature up to3 hours and then leveled off under constant concentration of acrylic acid and CAN. The activation energy was calculated to be 2.24kcal/mol in the initial stage of graft copolymerization.

Ceric ammonium nitrate(CAN)을 촉매로 하여 chitin으로 부터 유도한 chitosan에 아크릴산 단량체를 그라프트 공중합 하였다. 그라프트 공중합체의 확인은 IR 스펙트럼과 전자현미경으로 행하였다. 2g의 chitosan을 녹인 15wt.%-초산용액 에 아크릴산의 농도(0.370M)를 일정하게 하고 CAN의 농도를 변화시켰을 때 CAN의 농도가 3.33×10^-3M에 이를 때까지는 단량체 그라프트율(φ)이 증가하였으나 그 이상에서는 변화가 없었으며, CAN의 농도를 일정(3.33×10^-3M)하게 유지하고 단량체의 초기농도를 바꾸었을때 단량체의 농도가 0.370M이 될때 까지는 중량증가율(ΔW)과 Mv값이 직선적으로 증가하였으나 그 이상에서는 변화가 거의 없었다. 반응온도를 30, 40, 50℃로 각각 변화시키면서 단량체의 농도(0.370M)와 CAN의 농도(3.33×10^-3M)를 일정하게 유지하였을때, 반응시간에 대한 그라프트율(φ)은 반응온도가 높올수록 높았으나 반응시간 3시간 까지는 온도차와는 관계없이 모두 직선적으로 증가하였으며 그 이상에서는 평형을 유지하였다. 또한 초기 그라프트 공중합 단계 ( 2.5시간)에서의 활성화 에너지는 2.24kca1/mol이다.

Keywords: