Article
  • Linear Viscoelastic Properties of Rubber Modified Thermoplastic
  • Shin GS, Kim YJ, Kim CK, Kim JH, Kim BK
  • 고무개질 열가소성 수지의 선형점탄성
  • 신귀숙, 김영진, 김창기, 김준형, 김병규
Abstract
Melt blends of SAN(styrene-co-acrylonitrile) with SAN-graft-polybutadiene( PB) rubber were prepared using a Brabender Plasticorder. Melt state as well as solid state linear viscoelastic properties were measured using an RDS rheometer. With rubber addition, melt viscosity increased drastically, with yield at ≥20wt% rubber content, together with the increased pseudoplasticity at high frequencies. The lower glass transion temperature (Tg) and the higher Tg of g-ABS were respectively decreased and increased with narrowed transition zone in the blends. This phenomenon was interpreted in terms of graft SAN-PB phase separation.

SAN(styrene-co-acrylonitrile)과 SAN-graft-polybutadiene(PB) (g-ABS)을 Brabender Plasticorder에서 용융 블렌드 하여, 이들의 용응상태 및 고체 상태에서의 선형점탄성 거동을 RDS rheometer로 측정하였다. SAN에 g-ABS가 첨가됨에 따라 초기점도가 현저히 증가하였으며. 특히 g-ABS≥20wt%에서 항복거동을 나타내었고, 높은 진동주파수 범위에서는 의소성이 뚜렷하게 증가하였다. 또한 SAN/g-ABS 블렌드에서 SAN의 함량이 증가함에 따라 g-ABS의 lower Tg는 일률적으로 감소하는 경향을, higher Tg는 다소 증가하는 경향을 보였으며, 이를 SAN 첨가에 따른 g-ABS의 graft SAN-PB 상분리로 해석하였다.

References
  • 1. Munstedt H, Polym. Eng. Sci., 21, 259 (1981)
  •  
  • 2. Greco R, Mancerella C, Martuscelli E, Ragosta G, Polym. Eng. Sci., 28, 1922 (1987)
  •  
  • 3. Greco R, Mancerella C, Martuscelli E, Ragosta G, Polym. Eng. Sci., 28, 1929 (1987)
  •  
  • 4. Coppola F, Geco R, Murtuscelli E, Polymer, 28, 47 (1987)
  •  
  • 5. vanGisbergen JGM, Meijer HEH, Lemstra PJ, Polymer, 30, 2153 (1989)
  •  
  • 6. Wu S, Polymer, 26, 1855 (1985)
  •  
  • 7. Borggreve RJM, Gaymans RJ, Schuijer J, Polymer, 28, 1489 (1987)
  •  
  • 8. Borggreve RJM, Gaymans RJ, Polymer, 30, 63 (1989)
  •  
  • 9. Fowler ME, Keskkula H, Paul DR, Polymer, 28, 1703 (1987)
  •  
  • 10. Fowler ME, Keskkula H, Paul DR, J. Appl. Polym. Sci., 35, 1563 (1988)
  •  
  • 11. Donald AM, Kramer EJ, J. Mater. Sci., 17, 1765 (1982)
  •  
  • 12. White JMPrinciple of Polymer Engineering Rheology, Wiley Interscience, New York (1990)
  •  
  • 13. Aoki Y, Nihon Reoroji Gakkaishi, 7, 20 (1979)
  •  
  • 14. Bird RB, Armstrong RC, Hassager ODynamics of Polymeric Liquids, Vol. 1, Wiley, New York (1987)
  •  
  • 15. Vinogradov GV, Malkin AYRheology of Polymers, Spring-Verlag, New York (1980)
  •  
  • 16. Tadmor Z, Gogos CGPrinciples of Polymer Processing, Wiley, New York (1979)
  •  
  • 17. Han CDMultiphase Flow in Polymer Processing, Academic, New York (1981)
  •  
  • 18. Utracki LACurrent Topics in Polymer Science, Vol. 2, Hanser, New York (1987)
  •  
  • 19. VanOene H, J. Colloid Interface Sci., 40, 448 (1972)
  •  
  • 20. Utracki LA, J. Elastomer Plast., 18, 177 (1986)
  •  
  • 21. Ferry JDViscoelastic Properties of Polymers, 2nd ed., Wiley, New York (1980)
  •  
  • 22. Kim BK, Lee YH, Jeong HM, J. Appl. Polym. Sci., 40, 1805 (1990)
  •  
  • 23. Paul DR, Newman SPolymer Blends, Vol. 1, Academic Press, New York (1978)
  •  
  • 24. Rutkowska M, Macromolecules, 17, 821 (1984)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1992; 16(2): 160-165

    Published online Mar 25, 1992