  • Synthesis and Photochemical Properties of Water Soluble Photosensitive Polymer Based on Poly( vinyl alcohol)
  • Park LS, Han YS
  • 폴리비닐알콜에 감광성기를 도입한 수용성 감광성 고분자의 합성 및 감광특성
  • 박이순, 한윤수
Abstract
Photosensitive compounds, 1-methy1-4-[2-(4-formylpheny1) ethenyl] pridinium methosulfate (SbQ salt) and 1-methyl-4-[2-(4-diethylacetylpheny1) etheny1] pridinium methosulfate (SbQ-A salt), were synthesized from dimethy1 sulfate, terephthalaldehyde mono-(diethyl acetal) and 4-picoline. The structure of SbQ and SbQ-A salt were confirmed by FT-IR, 1H-NMR and GC-mass spectrometer. SbQ or SbQ-A salts were reacted with poly (vinyl alcohol), (PVA) in aqueous solution with acid catalyst to give photosensitive PVA-SbQ. The photocrosslinking reaction of PVA-SbQ was also studied with UV absorption spectrophotometer. As more SbQ-A was added in the reaction mixture, non-linearity between the amount of bound SbQ group and added SbQ-A salt was observed above 2.09 mol% SbQ group in PVA-SbQ due to viscosity build-up in the medium.

광 이량화 특성을 나타내는 1-methyl-4-[2-(4-formylpheny1)ethenyl] pridinium methosulfate (SbQ염)와 1-methyl-4-[2-(4-diethylacetylphenyl)ethenyl] pridinium methosulfate(SbQ-A염)를 dimethyl sulfate, terephthalaldehyde mono-(diethyl acetal) 및 4-picoline을 이용하여 합성하였다. 합성된 SbQ 및 SbQ-A염은 FT-IR, 1H-NMR, 자외 흡광 분광기를 이용하여 구조확인을 하였으며 자체의 감광특성을 조사하였다. 수용액에서 산촉매를 사응하여 SbQ 혹은 SbQ-A염을 PVA 측쇄에 도입하여 PVA-SbQ를 합성하였으며 광가교 특성을 조사하였다. PVA-SbQ의 합성에 있어서 반응물로 사용된 SbQ-A염의 함량과 PVA내 도입량 사이의 관계는 도입량 증가에 따른 반응계의 점도증가에 의해 2.09 mol% 이상부터는 비선형성을 나타내었다. 또 자외선 흡수 분광법으로써 합성된 PVA-SbQ내의 SbQ 도입량을 정량하였다.

Keywords: stilbazolium compounds; PVA-SbQ; phtodimerization; synthesis of photosensitive polymer

References
  • 1. Patent is pending on part of this paper 특허출원 95-5821
  •  
  • 2. Patent is pending on part of this paper 특허출원 95-5822
  •  
  • 3. Reiser APhotoreactive Polymers; The Science and Technology of Resists, A Wiley-Interscience Publication, New York (1989)
  •  
  • 4. DeForest WSPhotoresist; Materials and Process, Kingsport Press (1975)
  •  
  • 5. Ichimura K, Watanabe S, J. Polym. Sci. C: Polym. Lett., 18, 613 (1982)
  •  
  • 6. Ichimura K, Watanabe S, J. Polym. Sci. A: Polym. Chem., 20, 1419 (1982)
  •  
  • 7. Ichimura K, J. Polym. Sci. A: Polym. Chem., 20, 1411 (1982)
  •  
  • 8. Ichimura K, J. Polym. Sci. A: Polym. Chem., 22, 2817 (1984)
  •  
  • 9. Ichimura KU.S. Patent, 4,269,941 (1981)
  •  
  • 10. 特許出願公開, 昭 55-24126
  •  
  • 11. 特許出願公開, 昭 55-62446
  •  
  • 12. 特許出願公開, 平 2-148536
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1995; 19(5): 715-721

    Published online Sep 25, 1995