  • Charge Formation in Epoxy/Filler Composites
  • Nam JH, Lee CR, Suh KS, Kang DP
  • 에폭시/충전제 복합재료의 공간전하 형성
  • 남진호, 이창용, 서광석, 강동필
Abstract
Charge formation in epoxy loaded with filters such as SiO2, CaCO3 and Al(OH)3 was investigated. A small amount of homocharge was observed in the cured epoxy. The homocharge in epoxy/filler composite increased when both SiO2 and Al(OH)3 are mixed, whereas it decreased when CaCO3 is mixed. The highest homocharge was found in the epoxy containing 50 phr of SiO2. Space charge characteristics did not change by the surface treatment of SiO2 with γ-glycidoxypropyltrimetho- xysilane, a coupling agent, although diffused charge distributions were observed at some contents of coupling agent. Homocharge accumulation in these samples was attributed to the trapping of injected electrons at the epoxy/filler interfaces.

충전제의 종류를 SiO2, CaCO3, Al(OH)3로 변화시킨 에폭시/충전제 복합재료의 전하축적 현상을 살펴보았다. 연구결과 충전제를 사용하지 않은 에폭시에서는 동종전하가 형성되며 SiO2와 Al(OH)3 혼합에 따라 축적되는 동종전하의 양이 증가하였다. 그러나 CaCO3를 충진시킨 복합재료에서는 동종전하량이 감소하였다. SiO2를 충진시킨 복합재료에서는 50phr에서 축적되는 전하량이 가장 크게 나타났으며 50phr 이상의 SiO2 혼합에 따라 전하량은 감소하였다. 계면결합제인 γ-glycidoxypropyltrimethoxysilane으로 표면처리한 SiO2를 충진시킨 복합재료에서 축적되는 전하분포가 약간 넓게 측정되었으나 표면처리에 의해 전하축적현상이 변화하지 않았다. 이들 시편에서 동종전하 축적은 주입된 전자가 에폭시/충진제의 계면으로 트랩됨에 기인하는 것으로 생각된다.

Keywords: epoxy; filler; charge formation; interface; coupling agent

References
  • 1. 장인범, 신철기, 정일형, 박건호, 이준웅경화시간에 따른 에폭시 복합체의 TSC 특성, 한국전기전자재료학회 춘계학술대회, 212 (1995)
  •  
  • 2. Zee RH, Huang YH, Chen JJ, Jang BZ, Polym. Compos., 10, 205 (1989)
  •  
  • 3. 이덕진, 김명호, 김경환, 심종탁, 손인환, 김재환상호침입방목 에폭시수지의 교류 절연파괴특성 및 기계적특성, 한국전기전자재료학회 추계학술대회, 320 (1995)
  •  
  • 4. 홍능표, 조돈찬, 박홍규, 소병문, 김왕곤, 홍진웅전자선 조사된 에폭시 수지의 절연파괴 특성, 대한전기학회 추계학술대회, 430 (1995)
  •  
  • 5. Li Y, Takada T, Miyata H, Niwa T, J. Appl. Phys., 74, 2725 (1993)
  •  
  • 6. Suh KS, Lee JJ, Kim JY, Takada TCharge Formation in PE/Ethylene-Based Copolymer Laminates, Proc. 8th Int. Symp. High Voltage Engineering, 111 (1993)
  •  
  • 7. Suh KS, Noh HS, Lee MKInterfacial Conditions and Space Charge in PE Laminates, Proc. 1995 Int. Symp. Electr. Insul. Matls, 247 (1995)
  •  
  • 8. Tanaka T, Hayashi S, Shibayama K, J. Appl. Phys., 48, 3478 (1977)
  •  
  • 9. Yin W, Tanaka J, Damon DH, IEEE Trans. Dielectr. Insul., DEI1, 169 (1994)
  •  
  • 10. Jeffery AM, Damon DH, IEEE Trans. Dielectr. Insul., DEI2, 394 (1995)
  •  
  • 11. Suh KS, Lee HJ, Lee DS, Kang CG, IEEE Trans. Dielectr. Electr. Insul., DEI2, 460 (1995)
  •  
  • 12. Suh KS, Kim JY, Lee CR, Takada T, IEEE Trans. Dielectr. Electr. Insul., DEI3 (1996)
  •  
  • 13. Li Y, Yasuda M, Takada T, IEEE Trans. Dielectr. Electr. Insul., DEI1, 188 (1994)
  •  
  • 14. Suh KS, Hwang SJ, Noh JS, Takada T, IEEE Trans. Dielectr. Electr. Insul., DEI-1, 1077 (1994)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2023 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1996; 20(4): 633-638

    Published online Jul 25, 1996