  • Influence of Activation Temperature on Surface Structure Changes and Adsorption Properties of PAN-based Carbon Fibers
  • Park SJ, Kim KD
  • PAN계 탄소섬유의 활성화 온도에 따른 표면구조의 변화 및 흡착 특성
  • 박수진, 김기동
Abstract
In this work a series of activated carbon fibers have been prepared by CO2 activation of oxidized PAN-based carbon fibers at 700, 800, 900 and 1000 ℃ for 2 hrs, respectively. The adsorption properties of the activated carbon fibers(ACFs) were studied as a function of the heat treatment temperature(HTT). The ACFs were characterized by N2 gas adsorption and pH value and acid-base values of the carbon surfaces. As a result, ACFs showed different BET surface areas, total pore volumes and pore size distributions, depending on activation conditions. Among them, the condition derived from temperature at 1000 ℃ for 2 hrs gave the highest BET surface area, total pore volume. When the activation temperature was less than 800 ℃, the surface of ACFs have been developed in acidic nature, but basic properties have increased in increasing the HTT at higher than 900 ℃.

본 연구에서는 산화 처리된 PAN계 탄소섬유를 사용하여 700, 800, 900 및 1000℃의 온도로 2시간동안 CO2를 유입 기체로 하여 각각 활성화시켰다. 이렇게 제조된 활성 탄소섬유의 흡착 특성을 활성화 온도에 따라 연구하였다. 활성 탄소섬유의 표면 특성은 N2 기체 흡착에 따라 측정하였으며, 그 표면 성질은 pH 및 Boehm의 선택중화법에 따른 표면 산도 및 표면 염기도를 측정하였다. 활성 탄소섬유의 BET 비표면적, 총 기공 부피 및 기공 크기 분포도 등은 활성화 온도에 따라 많은 차이를 나타내었으며, 본 실험의 활성화 조건 중 1000℃에서 활성화시킨 활성 탄소섬유의 BET 비표면적, 총 기공 부피가 가장 큰 것으로 나타났다. 또한 활성화 온도는 활성 탄소섬유의 표면 성질에도 많은 영향을 주는데 활성화 온도가 800℃ 이하인 경우 활성 탄소섬유의 표면 성질은 약한 산성을 띠며, 900℃ 이상의 고온에서 활성화된 활성 탄소섬유는 염기성을 나타내었다.

Keywords: carbon fiber; activation; adsorption property; surface property

References
  • 1. Donnet JB, Bansal RCCarbon Fibers, Marcel Dekker, New York (1990)
  •  
  • 2. Chan WC, Die Angew. Makro. Chem., 213, 3724 (1993)
  •  
  • 3. Park SJ, Donnet JB, J. Colloid Interface Sci., 200(1), 46 (1998)
  •  
  • 4. Suzuki M, Carbon, 32, 577 (1994)
  •  
  • 5. Ermolenko IN, Lyubliner IP, Gulko NVChemically Modified Carbon Fibers, VCH, Weinheim (1990)
  •  
  • 6. Dubinin MMProgress in Surface and Membrane Science, Academic Press, New York (1975)
  •  
  • 7. Park SJ, Brendle M, J. Colloid Interface Sci., 188(2), 336 (1997)
  •  
  • 8. Polovina M, Babic B, Kaluderovic B, Dekanski A, Carbon, 35, 1047 (1997)
  •  
  • 9. Biniak S, Szymanski G, Siedlewski J, Swiatkoeski A, Carbon, 35, 12 (1997)
  •  
  • 10. Barton SS, Evans MJB, Hallilop E, Macdonald JAF, Carbon, 35, 1361 (1997)
  •  
  • 11. Leng CC, Pinto NG, Carbon, 35, 1375 (1997)
  •  
  • 12. Jaroniec M, Madey RPhysical Adsorption on Heterogeneous Solids, Elsevier, Amsterdam (1988)
  •  
  • 13. Boehm HP, Heck W, Sappok R, Angew. Chem., 76, 742 (1964)
  •  
  • 14. Brunauer S, Emmett PH, Teller E, J. Am. Chem. Soc., 60, 309 (1938)
  •  
  • 15. Barrett EP, Joyner LG, Halenda PP, J. Am. Chem. Soc., 73, 373 (1951)
  •  
  • 16. Bansal RC, Donnet JB, Stoeckli FActive Carbon, Marcel Dekker, New York (1988)
  •  
  • 17. Leony Leon CA, Solar JM, Calemma V, Radovic LR, Carbon, 30, 797 (1993)
  •  
  • 18. Sing KSW, Everett DH, Haul RAW, Pure Appl. Chem., 57, 603 (1985)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1998; 22(6): 994-998

    Published online Nov 25, 1998