  • The Impact Fracture Behaviors of Low Density 2-D Carbon/Carbon Composites by Drop Weight Impact Test
  • Joo HJ, Son JS
  • 낙하 충격 시험에 의한 저밀도 2-D 탄소/탄소 복합재의 충격파괴거동
  • 주혁종, 손종석
Abstract
In this study, the fracture behavior by low velocity impact damage and the tendencies of impact energy absorption were investigated. Low velocity impact tests were performed using a mini tower drop weight impact tester, and graphite powder, carbon black and milled carbon fiber were chosen as additives. Addition of graphite powder increased the maximum load and maintained the stress long until the total penetration happened. At the content of 9 vol%, they showed the maximum of 42% improvement in impact strength compared composites containing no additives. At the test with low impact energy of 0.4 J, impact energy was consumed by delamination in the composite containing no additives, however, as graphite contents increased, the tendency of failure changed to the penetration of the specimen.

저밀도 2-D 탄소/탄소 복합재료의 저속 충격에 의한 파괴 거동과 첨가제에 따른 충격 에너지 흡수 경향을 연구하였다. 저속 충격시험은 mini tower 낙추 충격 시험기를 이용하였으며, 흑연, 카본블랙, 분쇄탄소섬유를 첨가제로 선택하였다. 흑연의 첨가는 최대하중값을 증가시켰으며, 전체적인 관통이 일어나기까지 응력을 오랫동안 유지시키는 효과를 나타내었다. 특히 9 vol%의 함량에서 흑연이 첨가되지 않은 시편보다 약 42%의 충격 흡수 개선을 보였다. 약 0.4 J의 낮은 충격에너지에 의한 충격 회수에 따른 실험에서 첨가제가 첨가되지 않은 시편의 경우, 충격에너지는 층간분리에 의해 소모되고, 흑연의 함량이 증가함에 따라 파괴 경향은 시편의 관통으로 변화함을 관찰할 수 있었다.

Keywords: carbon/carbon composites; low velocity Impact test; impact energy; delamination; penetration

References
  • 1. Lim SK, Luck Polymer Tech., 2, 71 (1987)
  •  
  • 2. Saimders DEJ, Soutis C, Kinsey A, Composities, 26, 661 (1995)
  •  
  • 3. Prevorsek DC, Chin HB, Bhatnagar A, Compos. Structures, 23, 137 (1993)
  •  
  • 4. Yurgartis SW, Macgibbon BS, Mulvaney P, J. Mater. Sci., 27, 6679 (1992)
  •  
  • 5. Hong DH, Luck Polymer Tech., 5, 40 (1988)
  •  
  • 6. Lee SY3rd Conference on National Defes Materials C-102 (2000)
  •  
  • 7. Maikuma H, Gillespie JW, Wilkins DJ, Compos. Mater., 24, 124 (1990)
  •  
  • 8. Jun EJ, Compos. Mater., 26, 2247 (1992)
  •  
  • 9. Mcquillen EJ, Gause LW, Compos. Mater., 10, 79 (1976)
  •  
  • 10. Ma CC, Tai NH, Wu GY, Lin SH, Lin JM, Ong CL, Chang YC, Sheu MFANTEC '96 Preceeding, 917 (1996)
  •  
  • 11. Zhou G, Compos. Structures., 31, 185 (1995)
  •  
  • 12. Kim BJ, Choo MJ, Kang TJ, J. Korea Compos. Mater., 4, 1 (1991)
  •  
  • 13. Son JS, Chung KH, Joo HJ, Polym.(Korea), 24(6), 845 (2000)
  •  
  • 14. Choi IH, Choi YR, Hong CS, J. Korea Compos. Mater., 6, 69 (1993)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2002; 26(2): 270-278

    Published online Mar 25, 2002

  • Received on Dec 21, 2001
  • Accepted on Feb 19, 2002