The mechanical properties of particulate filler composites prepared from the glass beads having the average radius (R) and unsaturated polyester matrix were investigated. The results show that, when glass beads were treated with the coupling agent, the experimentally derived Young''s modulus and tensile strength of the comosites were increased higher than those theoretical values at the same volume fraction of glass beads, and then experimental values were increased proprtionally to the increasing ratio of surface area. By applying the coefficient of surface area S to the Kerner and Nielsen''s equation at 15% of filler content, the following relations were derived experimentally; log(R^-1)=aSm-b, in Young''s modulus. log(R^-1)=a''logSt+b, in tensile strength.

불포화 polyester matrix에 각각의 반경(R)을 갖는 glass beads를 충전시켜 입상분산계 복합계를 제작하고 물리적 성질을 검토한 결과 충전재의 동일체적분율에서 glass beads의 표면을 coupling agent로 처리했을 때 복합계의 탄성율과 인장강도는 이론값 보다 큰 값을 표시했고, 충전재의 체표면적증가율과 비례적으로 증가했다. 이와 같은 비례적 관계를 충전함량 15%에서 Kerner와 Nielson의 이론식에 면적계수 S를 도입하여 실험적으로 산출하여 다음과 같은 관계를 얻었다. 탄성율에서 log(R^-1)=_aS_m-b, 인장강도에서 log(R^-1)=a''logS_t+b''. 여기서,(S_m 및 S_t는 각각 탄성율과 인장강도에서의 면적계수,)(R^-1)은 충전재의 체표면적증가율, a,b와 a'',b''는 Polymer matrix와 충전재의 종류 및 계면접착력에 의해 결정되는 실험정수이다.