  • Fabrication of a Film Coated with Conducting Polymer Using One Atmospheric Pressure Plasma
  • Jung JS, Yang IY, Myung SW, Choi HS, Kim JH
  • 대기압 플라즈마를 이용한 전도성 고분자 코팅 필름 제조
  • 정진석, 양인영, 명성운, 최호석, 김종훈
Abstract
A composite film of polyurethane(PU)-graft-poly(acrylic acid)(PAAc)/polyaniline (PU-g-AAc/PANI) was successfully fabricated for the purpose of adding conductivity on the surface of a general purpose polymer and improving adhesive property between the general purpose polymer and conducting polymer layer. The results from ATR-FTIR and XPS analyses also supported the successful synthesis of the composite film by showing characteristic peaks for every step. A low surface resistivity of 2×103 ohm/sq proved the surface conductivity of synthesized PU-g-AAc/PANI film and the surface resistance decreased with increasing the amount of grafted AAc, which acted as a dopant for PANI film.

범용 고분자 표면에 전도성 부여와 범용 고분자와 전도성 고분자층의 접합력 향상을 목적으로 폴리우레탄 (PU)-graft-poly(acrylic acid)(PAAc)/폴리아닐린(PU-g-AAc/PANI) 복합체 필름을 제조하였다. ATR-FTIR과 XPS분석 결과, 각 처리 절차에 대응하는 특성피크를 관찰하였고, 이를 통하여 각 단계의 실험이 성공적으로 수행되었음을 확인할 수 있었다. 표면저항을 측정한 결과, 2×103 ohm/sq으로 절연성인 폴리우레탄 필름에 전도도가 부여됨을 알 수 있었고, PU-g-AAc/PANI 필름에서 폴리아닐린에 대한 도판트 역할을 하는 아크릴산의 양이 증가할수록 표면저항은 감소함을 알 수 있었다.

Keywords: atmospheric pressure plasma; polyurethane film; conducting polymer; acrylic acid; polyaniline

References
  • 1. Ma ZH, Han HS, Tan KL, Kang ET, Neoh KG, Int. J. Adhes. Adhes., 19, 359 (1999)
  •  
  • 2. Fu Y, Elsenbaumer RL, Chem. Mater., 6, 671 (1994)
  •  
  • 3. Laska J, J. Mol. Struct., 701, 13 (2004)
  •  
  • 4. Chen YJ, Kang ET, Neoh KG, Tan KL, Polymer, 41(9), 3279 (2000)
  •  
  • 5. Chen SA, Lee HT, Macromolecules, 28(8), 2858 (1995)
  •  
  • 6. Xie HQ, Xiang Q, Eur. Polym. J., 36, 509 (2000)
  •  
  • 7. Pud A, Ogursov N, Korzhenko A, Shapoval G, Prog. Polym. Sci, 28, 1701 (2003)
  •  
  • 8. Fu Y, Weiss RA, Synth. Met., 84, 129 (1997)
  •  
  • 9. Zhang H, Li C, Synth. Met., 44, 143 (1991)
  •  
  • 10. Wan M, Yang J, J. Appl. Polym. Sci., 49, 1639 (1993)
  •  
  • 11. Yang IY, Myung SW, Choi HS, Kim IH, Polym.(Korea), 29(6), 581 (2005)
  •  
  • 12. Yeom YH, Myung SW, Choi HS, Korean Chem. Eng. Res., 42(1), 89 (2004)
  •  
  • 13. Lei J, Liao X, Eur. Polym. J., 37, 771 (2001)
  •  
  • 14. Aliev R, Garcia P, Burillo G, Radiat. Phys. Chem., 58, 299 (2000)
  •  
  • 15. Park SJ, Jin JS, J. Korean Ind. Eng. Chem., 11(7), 762 (2000)
  •  
  • 16. Lu J, Li J, Ha H, Radiat. Phys. Chem., 60, 625 (2001)
  •  
  • 17. Matsumoto A, Mitomi D, Aota H, Ikeda J, Polymer, 41(4), 1321 (2000)
  •  
  • 18. Zhong WB, Yang YS, Yang WT, Thin Solid Films, 479(1-2), 24 (2005)
  •  
  • 19. Hu HL, Saniger JM, Banuelos JG, Thin Solid Films, 347(1-2), 241 (1999)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2007; 31(4): 308-314

    Published online Jul 25, 2007

  • Received on Jan 25, 2007
  • Accepted on May 16, 2007