  • Synthesis and Swelling Characteristics of Poly(N-isopropylacrylamide) Containing Polydimethylsiloxane and Nano Clay
  • Nho HC, Lee CW, Park S, Yoon KS
  • Nano Clay와 Polydimethylsiloxane을 포함하는 Poly(N-isopropylacrylamide) 공중합체의 합성과 팽윤거동
  • 노휘철, 이찬우, 박상윤, 윤구식
Abstract
Poly(N-isopropylacrylamide)(PNIPAAm) containing polydimethylsiloxane(PDMS) block and nano clay was obtained by the polymerization of NIPAAm and [3-(methacryloylamino)propyl]trimethyl ammonium montmorillonite(MAPTAC-MMT) with PDMS-macroinitiator. The polymer was characterized with FT-IR, XRD and DSC. The addition of PDMS in the polymers did not affect the value of the lower critical solution temperature(LCST) and the glass transition temperature(Tg) of the PNIPAAm. However, the swelling ratio decreased with increasing PDMS contents. In the case of PNIPAAm containing nano clay, the content of MAPTAC-MMT did not affect swellability, but the Tg of the PNIPAAm decreased with increasing nano clay contents.

Polydimethylsiloxane(PDMS) macroinitiator를 이용하여 N-isopropylacrylamide(NIPAAm)와 [3- (methacryloylamino)propyl]trimethyl ammonium montmorillonite(MAPTAC-MMT)를 중합하여 주사슬에 PDMS 블록을 가지며 nano clay(montmorillonite)를 가진 PNIPAAm 중합체를 합성하여 FT-IR과 XRD를 이용하여 확인하고 DSC를 이용하여 열적 성질을 조사하였으며 중합체의 온도에 따른 수팽윤도를 구하였다. DSC 측정 결과 poly(NIPAAm-b-PDMS) 속의 PNIPAAm과 PDMS는 분리된 상으로 존재했으며, 소수성인 PDMS의 함량이 증가함에 따라 수팽윤도는 감소하였으나 LCST 값은 큰 변화가 없었다. 또한, PNIPAAm의 유리전이온도 (Tg)는 분리된 상으로 인해 큰 변화가 없었다. 또한, 나노입자의 첨가는 전반적으로 수팽윤도에는 영향을 주지 않았으나 중합체의 Tg의 값은 감소하였다.

Keywords: N-isopropylacrylamide; montmorillonite; polydimethylsiloxane; thermo-reversible; swelling

References
  • 1. Schild HG, Prog. Polym. Sci., 17, 163 (1992)
  •  
  • 2. Hirokawa Y, Tanaka T, J. Chem. Phys., 81, 6379 (1984)
  •  
  • 3. Cho HK, Kim BS, Noh ST, Polym.(Korea), 25(2), 186 (2001)
  •  
  • 4. Du J, Peng YX, Zhang TT, Ding XB, Zheng ZH, J. Appl. Polym. Sci., 83(14), 3002 (2002)
  •  
  • 5. Zhang XZ, Yang YY, Wang FJ, Chung TS, Langmuir, 18(6), 2013 (2002)
  •  
  • 6. Okano T, Bae YH, Kim SW, J. Control. Release, 11, 255 (1990)
  •  
  • 7. Park YS, Han HD, Hong SU, Kim SS, Shin BC, Polym.(Korea), 28(1), 59 (2004)
  •  
  • 8. Takezawa T, Mori Y, Yoshizato K, Biotechnology, 8, 854 (1990)
  •  
  • 9. Takeuchi S, Omodaka I, Makoromol. Chem., 194, 1991 (1993)
  •  
  • 10. Holtz JH, Asher SA, Nature, 389(6653), 829 (1997)
  •  
  • 11. Kim K, Shin YJ, Polym.(Korea), 18(6), 1048 (1994)
  •  
  • 12. Most CF, J. Biomed. Mater. Res., 6, 3 (1972)
  •  
  • 13. Lacey RE, Cowar DRControlled Release of Biologically Active Agents, Plenum Press, New York, Chap. 5 (1974)
  •  
  • 14. Lee C, Ulman KL, Larson KR, Drug Dev. Ind. Pharm., 12, 369 (1986)
  •  
  • 15. Chien YW, Lambert HJ, Grant DE, J. Pharm. Sci., 63, 365 (1974)
  •  
  • 16. Ross-Murpy SB, Todd S, Polymer, 24, 481 (1983)
  •  
  • 17. Ramaraj B, Radhakrishnan G, J. Appl. Polym. Sci., 51(6), 979 (1994)
  •  
  • 18. Chen H, Hsieh YL, J. Polym. Sci. A: Polym. Chem., 42(13), 3293 (2004)
  •  
  • 19. Kim JP, Lyu SG, Bae KS, Sur GS, Polym.(Korea), 25(2), 263 (2001)
  •  
  • 20. Yano K, Usuki A, Okada A, Kurauchi T, Kamigaito O, J. Polym. Sci. Part A: Polym. Chem., 31, 2493 (1993)
  •  
  • 21. Blumstein A, J. Polym. Sci. Part A: Polym. Chem., 3, 2653 (1965)
  •  
  • 22. Bignotti F, Sartore L, Penco M, Ramorino G, Peroni I, J. Appl. Polym. Sci., 93(4), 1964 (2004)
  •  
  • 23. Shibayama M, Suda J, Karino T, Okabe S, Takehisa T, Haraguchi K, Macromolecules, 37(25), 9606 (2004)
  •  
  • 24. Bellamy LJThe infra-red spectra of complex molecules, Chapman and Hall, London, p 244 (1975)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2010; 34(2): 166-171

    Published online Mar 25, 2010

  • Received on Nov 17, 2009
  • Accepted on Jan 6, 2010