  • Effects of Thermal and Electrical Conductivity of Al(OH)3 Functionalized Graphene/Epoxy Composites by Simple Sol-Gel Method
  • Kim J, Im H, Han J, Kim J
  • 졸-젤 법을 이용한 Al(OH)3 처리된 그래핀/에폭시 복합체의 열 및 전기전도 특성 분석
  • 김지원, 임현구, 한중근, 김주헌
Abstract
Functionalized graphene/epoxy composites were prepared to miprove thermal conductivities of epoxy composites and to maintain electrical insulating property. Graphene oxide (GO) was prepared using Hummers method, and then GO was reacted with aluminum isopropoxide to functionalize Al(OH)3 layer onto GO surface by a simple sol-gel method (Al-GO). GO and Al-GO were characterized by X-ray photoelectron spectroscopy, field emission scanning electron microscopy and transmission electron microscopy. The analyses confirm that GO was coated with a large and dense coverage of Al(OH)3. GO and Al-GO (1 and 3 wt%) were embedded in bisphenol A (DGEBA) to investigate the effects of electrical insulating property. Electrical resistivity showed that Al-GO had better insulating property than GO. Further, the thermal conductivity of GO and Al-GO/epoxy composites was higher than that of neat epoxy resins. In particular, the thermal conductivity of Al-GO/bisphenol F (DGEBF) improved by 23.3% and Al-GO/DGEBA enhanced by 21.8% compared with pure epoxy resins.

그래핀의 우수한 열적 특성을 이용하여 에폭시 수지의 열전도 특성을 향상시키며 전기 절연성질을 유지하는 기능화된 그래핀/에폭시 복합체를 제작하여 전기 및 열전도도를 측정하였다. 기능화된 그래핀은 Hummers법을 이용하여 산화그래핀(GO)을 얻어낸 후 aluminum isopropoxide를 졸-젤 반응을 통해 Al(OH)3를 그래핀 표면에 도입하여 제작하였다(Al-GO). GO와 Al-GO의 기능화 여부 확인을 위하여 XPS, FE-SEM, FE-TEM 분석을 시행하였으며 GO 표면에 Al(OH)3 층이 생성된 것을 확인하였다. 기능화된 그래핀/에폭시 복합체는 bisphenol A(DGEBA) 계열의 에폭시에 1, 3 wt%의 GO와 Al-GO를 첨가하여 전기저항을 측정하였으며 Al-GO가 GO와 비교하여 전기절연성질이 우수하였다. 또한 DGEBA와 bisphenol F(DGEBF) 계열의 에폭시에 1 wt%의 GO와 Al-GO를 첨가하여 열전도 특성을 비교하였으며 순수 에폭시 레진과 비교하여 Al-GO/DGEBF는 23.3%, Al-GO/DGEBA는 21.8%의 열전도도 증가를 보였다.

Keywords: functionalized graphene; graphene oxide; epoxy; electrical resistivity; thermal conductivity.

References
  • 1. Bauer RS, Epoxy resins chemistry, American Chemical Society, Washington D.C. (1979)
  •  
  • 2. May CA, Epoxy Resins, Marcel Pekker, New York (1988)
  •  
  • 3. Kapur P, McVittie JP, Saraswat KC, IEEE Trans. Electron. Dev., 49, 590 (2002)
  •  
  • 4. Obreja VVN, IEEE Int. Symp. Indus. Electron-ISIE06., 2, 835 (2006)
  •  
  • 5. Balandin AA, Ghosh S, Bao W, Calizo I, Teweldebrhan D, Miao F, Lau CN, Nano Lett., 8, 902 (2008)
  •  
  • 6. Du X, Skachko I, Barker A, Andrei EY, Nature Nanotechnol., 3, 491 (2008)
  •  
  • 7. Lee CG, Wei XD, Kysar JW, Hone J, Science., 321, 385 (2008)
  •  
  • 8. Geng Y, Li J, Wang SJ, Kim JK, J. Nanosci. Nanotechnol., 8, 6238 (2008)
  •  
  • 9. Li D, Muller MB, Gilje S, Kaner RB, Wallace GG, Nature Nanotechnol., 3, 101 (2008)
  •  
  • 10. Imai T, Sawa F, Nakano T, OzaKi T, Shimizu T, Kozako M, Tanaka T, IEEE T. Dielectr. El. In., 13, 319 (2006)
  •  
  • 11. Xu Y, Chung DDL, Mroz C, Compos. Part A., 32, 1749 (2001)
  •  
  • 12. Sim LC, Ramanan SR, Ismail H, Seetharamu KN, Goh TJ, Thermochim. Acta, 430(1-2), 155 (2005)
  •  
  • 13. Stti A, Larpent P, Gun’ko Y, Carbon., 48, 3376 (2010)
  •  
  • 14. Ganguli S, Roy AK, Anderson DP, Carbon., 46, 806 (2008)
  •  
  • 15. Stankovich S, Dinkin DA, Piner RD, Kohlhaas KA, Kleinhammes A, Jia Y, Wu Y, Nguyen ST, Ruoff RS, Carbon., 45, 1558 (2007)
  •  
  • 16. Martin JM, Vovelle L, Bou M, Mogne TL, Appl. Surf. Sci., 47, 149 (1991)
  •  
  • 17. Beccaria AM, Castello G, Poggi G, Brit. Corros. J., 30, 283 (1995)
  •  
  • 18. Meenan BJ, Hewitt JA, Brown NMD, Surf.Interf. Anal., 18, 187 (1992)
  •  
  • 19. Hernadi M, Couteau E, Seo JW, Forro L, Langmuir, 19(17), 7026 (2003)
  •  
  • 20. Nylund A, Olefjord I, Surf. Interf. Anal., 21, 283 (1994)
  •  
  • 21. Stankovich S, Dikin DA, Dommett GHB, Kolhaas KM, Zimney EJ, Stach EA, Piner RD, Nguyen ST, Ruoff RS, Nature., 442, 282 (2006)
  •  
  • 22. Jung I, Dikin DA, Piner RD, Ruoff RS, Nano Lett., 8, 4283 (2008)
  •  
  • 23. Watcharotone S, Dikin DA, Stankovich S, Piner R, Jung I, Dommett GHB, Evmennenko G, Wu SE, Chen SF, Liu CP, Nguyen ST, Ruoff RS, Nano Lett., 7, 1888 (2007)
  •  
  • 24. Yasmin A, Daniel IM, Polymer, 45(24), 8211 (2004)
  •  
  • 25. Yang SY, Ma CCM, Teng CC, Huang YW, Liao SH, Huang YL, et al.,, Carbon., 48, 592 (2010)
  •  
  • 26. Lin C, Chung DDL, Carbon., 47, 295 (2009)
  •  
  • 27. Biercuk MJ, Llaguno MC, Radosavljevic M, Hyun JK, Johnson AT, Fischer JE, Appl. Phys. Lett., 80, 29767 (2002)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2012; 36(1): 22-28

    Published online Jan 25, 2012

  • Received on May 23, 2011
  • Accepted on Aug 11, 2011