  • Immobilization Metallocene Inside Surface-functionalized Nanopore of Micelle-Templated Silica and its Ethylene Polymerization
  • Lee JS, Yim JH, Ko YS
  • 표면 기능화된 Micelle-Templated Silica 나노세공 내 메탈로센 담지 및 에틸렌 중합
  • 이정숙, 임진형, 고영수
Abstract
A functionalization of mesoporous materials with organosilane was carried out via a post-synthesis grafting method and (n-BuCp)2ZrCl2/methylaluminoxane (MAO) as subsequently immobilized on the functionalized mesoporous materials for ethylene polymerization. Organosilanes having amine, cyano or imidazoline group such as N-[(3-trimethoxysilyl)propyl]ethylenediamine (2NS), 4-(triethoxysilyl)butyronitrile (1NCy), 1-(3-triethoxysilylpropyl)-2- imidazoline (2NIm) were used for the surface functionalization of mesoporous materials. In the SBA-15/2NS/(n-BuCp)2ZrCl2 catalyst preparation, the amount of MAO in feed increased with an decrease in the Zr content of the supported catalyst, and Al content in the supported catalyst increased. The ethylene homopolymerization activity of SBA-15/2NS/(n-BuCp)2ZrCl2 dramatically increased as the amount of MAO in feed increased. Furthermore, when the immobilization time was 6 hrs, SBA-15/2NS/(n-BuCp)2ZrCl2 showed the highest activity. The activities of supported 2NS-, 1NCy-, 2NIm-functionalized catalysts decreased in the following order, SBA-15/2NS/ > SBA-15/2NIm/ > SBA-15/1NCy/(n-BuCp)2ZrCl2. 2NS and 2NIm which have two amine groups per silane molecule were shown to interact with (n-BuCp)2ZrCl2 strongly compared to 1NCy which has one amine group. Thus, the activities increased with an increase in the nitrogen and the Zr content of the supported catalysts.

메조포러스 물질의 표면을 post-synthesis grafting method를 통해 표면을 기능화시킨 후 (n-BuCp)2ZrCl2/methylaluminoxane(MAO)를 담지하여 에틸렌 중합을 실시하였다. 아민기와 시안기를 가지는 유기실란 N-[(3-trimethoxysilyl)propyl]ethylenediamine(2NS), 4-(triethoxysilyl)butyronitrile(1NCy), 1-(3-triethoxysilylpropyl)-2-imidazoline(2NIm)는 메조포러스 물질의 표면 기능화에 사용되었다. SBA-15/2NS/(n-BuCp)2ZrCl2촉매 담지시 MAO의 양이 증가할수록 Zr 함량은 감소하였고 Al 함량은 증가하였다. 에틸렌 중합 활성은 MAO의 양이 증가할수록 급격히 증가함을 볼 수 있었다. 담지시간이 6시간일 때 가장 높은 활성을 보였다. 유기실란의 종류에 따른 활성 차이는 SBA-15/2NS/(n-BuCp)2ZrCl2 > SBA-15/2NIm/(n-BuCp)2ZrCl2 > SBA-15/1NCy/(n-BuCp)2ZrCl2 순으로 감소하였다. 아민기를 두 개 갖는 2NS와 2NIm은 아민기를 하나 갖는 1NCy보다 (n-BuCp)2ZrCl2와 더 강하게 상호작용을 한다. 따라서 촉매 내 질소와 Zr함량이 증가할수록 활성은 증가하였다.

Keywords: mesoporous material; surface functionalization; organosilane; metallocene; ethylene polymerization.

References
  • 1. Kresge CT, Leonowicz ME, Roth WJ, Vartuli JC, Beck JS, Nature., 359, 710 (1992)
  •  
  • 2. Beck JS, Vartuli JC, Roth WJ, Leonowicz ME, Kresge CT, J. Am. Chem. Soc., 114, 10834 (1992)
  •  
  • 3. Rodriguez I, Iborra S, Corma A, Rey F, Jorda JL, Chem. Commun., 7, 593 (1999)
  •  
  • 4. Stein A, Adv. Mater., 15(10), 763 (2003)
  •  
  • 5. Mbaraka IK, Radu DR, Lin VSY, Shanks BH, J. Catal., 219(2), 329 (2003)
  •  
  • 6. Dai S, Burleigh MC, Shin Y, Morrow CC, Barnes CE, Xue Z, Angew. Chem., Int. Ed. Engl., 38, 1235 (1999)
  •  
  • 7. Yoshitake H, Yokoi T, Tatsnmi T, Chem. Mater., 15, 1713 (2003)
  •  
  • 8. Lin VSY, Lai CY, Huang JG, Song SA, Xu S, J. Am. Chem. Soc., 123(46), 11510 (2001)
  •  
  • 9. Wang XG, Lin KSK, Chan JCC, Cheng SF, J. Phys. Chem. B, 109(5), 1763 (2005)
  •  
  • 10. Jessica MR, Mika L, Chem. Mater., 19, 5023 (2007)
  •  
  • 11. Chong ASM, Zhao XS, J. Phys. Chem. B, 107(46), 12650 (2003)
  •  
  • 12. Zhao XS, Lu GQ, J. Phys. Chem. B, 102(9), 1556 (1998)
  •  
  • 13. Zhao DY, Feng JL, Huo QS, Melosh N, Fredrickson GH, Chmelka BF, Stucky GD, Science, 279(5350), 548 (1998)
  •  
  • 14. Carrero A, Van Grieken R, Suarez I, Paredes B, Polym. Eng. Sci., 48(3), 606 (2008)
  •  
  • 15. Yokoi T, Yoshitake H, Tatsnmi T, J. Mater. Chem., 14, 951 (2004)
  •  
  • 16. Zhao XS, Lu GQ, Whittaker AJ, Millar GJ, Zhu HY, J. Phys. Chem., 101, 6525 (1997)
  •  
  • 17. Choudary BM, Kantam ML, Sreekanth P, Bandopadhyay T, Figueras F, Tuel A, J. Mal. Catal. A., 142, 361 (1999)
  •  
  • 18. Mercier L, Pinnavaia TJ, Environ. Sci. Technol., 32, 2749 (1998)
  •  
  • 19. Liu AM, Hidajat K, Kawi S, Zhao DY, Chem. Commun., 13, 1145 (2000)
  •  
  • 20. Brown J, Richer R, Mercier L, Micropor. Mesopor. Mater., 37, 41 (2000)
  •  
  • 21. Chao G, Dao Z, Guoxin J, Chinese Sci. Bull., 49, 249 (2004)
  •  
  • 22. Ko YS, Lee JS, Yim JH, Jeon JK, Jung KY, J. Nanosci. Nanotechnol., 10, 180 (2010)
  •  
  • 23. LI D, Sur GS, Polym.(Korea), 34(4), 289 (2010)
  •  
  • 24. Kim JY, Yoon SY, Yang YD, Noh SK, Polym.(Korea), 32(6), 566 (2008)
  •  
  • 25. Zhao D, Huo Q, Feng J, Chmelka BF, Stucky GD, J. Am. Chem. Soc., 120(24), 6024 (1998)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2012; 36(1): 111-116

    Published online Jan 25, 2012

  • Received on Oct 25, 2011
  • Accepted on Dec 6, 2011