  • Fabrication of High-Aspect-Ratio Microscale Polymer Hairs Having Surface Wrinkles
  • Park SH, Kim SJ, Park HJ, Lee JC, Shin BS
  • 고 세장비 표면주름을 가진 마이크로 폴리머 헤어 제작
  • 박상후, 김성진, 박희진, 이주철, 신보성
Abstract
We proposed a new process to fabricate a highaspect-ratio microhair having surface wrinkles using the contactand-tension of a microstamp. Through this work, we observed that regular surface wrinkles were generated on the hair with a diameter of around 20 μm due to the uni-directional compressive stress during the photocuring process by ultraviolet light. To do this, we conducted an experimental system setup for contactand-tension process. From the preliminary test results, we believed that the proposed method can be applied to make a long polymer hair having surface wrinkles for special applications to biomimetics, and some research fields related on surface area such as heat transfer and catalyst enhancement.

본 연구에서는 스탬프와 레진의 접촉-인장 방법을 이용하여 고 세장비를 가지는 폴리머 마이크로 헤어를 제작하는 공정을 제안하였다. 또한 광경화시 수축방향에 따라 마이크로헤어에 표면주름이 다르게 생성되는 것을 실험적으로 관찰하였으며, 헤어의 직경이 20 μm 부근일 때, 일정한 패턴을 가진 표면주름이 제작되었다. 이 직경에서 스탬프와 레진의 접합력보다 수축력이 더 크게 되어 광경화 도중에 레진이 스탬프에서 분리되면서 단방향의 수축을 유도하게 되어 일정한 간격의 주름이 발생하는 것으로 사료된다. 본 연구의 기초결과를 이용하여, 향후 균일한 표면주름을 가지는 다양한 형태의 마이크로 폴리머 헤어를 제작할 수 있을 것으로 사료되며, 생체모사, 열전달 및 촉매 촉진과 같은 표면적과 관련된 기술 등 다양한 분야에 응용이 가능할 것으로 사료된다.

Keywords: contact-and-tension method; high aspect ratio microhair; surface wrinkles; control of wrinkling direction.

References
  • 1. Porada H, Bouougri EH, Earth-Science Reviews., 81, 199 (2007)
  •  
  • 2. Khang DY, Jiang H, Huang Y, Rogers JA, Science., 311, 208 (2006)
  •  
  • 3. Lin PC, Yang S, Soft Matter., 5, 1011 (2009)
  •  
  • 4. Khare K, Zhou JH, Yang S, Langmuir, 25(21), 12794 (2009)
  •  
  • 5. Chung JY, Nolte AJ, Stafford CM, Adv. Mater., 23(3), 349 (2011)
  •  
  • 6. Harrison C, Stafford CM, Zhang W, Karim A, Appl.Phys. Lett., 85, 4016 (2004)
  •  
  • 7. Huang ZY, Hong W, Suo Z, J. Mech. Phys. Solids., 53, 2101 (2005)
  •  
  • 8. Im SH, Huang R, J. Mech. Phys. Solids., 56, 3315 (2008)
  •  
  • 9. Schaefer M, Jacobs P, Bauer D, Int. J. Adv. Manuf. Technol., 51, 935 (2010)
  •  
  • 10. Jeong HE, Lee JK, Kwak MK, Moon SH, Suh KY, Appl. Phys. Lett., 96, 043704 (2010)
  •  
  • 11. Ge L, Ci L, Goyal A, Shi R, Mahadevan L, Ajayan PM, Dhinojwala A, Nano Lett., 10, 4509 (2010)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2013; 37(1): 1-4

    Published online Jan 25, 2013

  • Received on Oct 8, 2012
  • Accepted on Nov 6, 2012