  • Polyimide Films Using Dianhydride Containing Ester Linkages and Various Amine Monomers
  • Choi CH, Chang JH
  • 에스터기를 가지는 무수물과 다양한 아민 단량체를 이용한 폴리이미드 필름
  • 최창훤, 장진해
Abstract
Hydroquinone bis(trimellitic anhydride) (HQ-TA) was synthesized from trimellitic anhydride chloride and hydroquinone. Poly(amic acid)s (PAAs) were synthesized by reacting a HQ-TA with six different diamines, which were cyclized to yield polyimides (PIs) containing ester linkages by chemical- and thermal-imidization methods. The various PIs were synthesized from structurally different aromatic diamines. The glass transition temperatures (Tg) were in the range of 167-215 ℃, and the decomposition temperatures (TDi) were in the range of 364-451 ℃. The maximum improvements in coefficient of thermal expansion (CTE) and barrier to oxygen permeation were observed in PIs using TFB (3.23 ppm/℃) and 4,4-ODA (<10^(-2) cc/m2/day), respectively. The PI films possessed a transmittance of 65.89% at 500 nm and had a yellowish color with a yellow index (YI) of 3.01-69.52.

Trimellitic anhydride chloride와 hydroquinone을 이용하여 hydroquinone bis(trimellitate anhydride)(HQ-TA)를 합성하였다. 합성된 HQ-TA와 6가지의 다양한 디아민들을 사용하여 전구체 polyamic acid(PAA)를 합성한 후, 열적-및 화학적-이미드화 반응을 거쳐 에스터 그룹을 가지는 폴리이미드(polyimide, PI) 필름을 합성하였다. PI 합성은 구조적으로 다양한 방향족 디아민을 사용하였다. 각 디아민 구조에 따른 유리전이온도(Tg)는 167-215 ℃를 보였고, 초기분해온도(TDi)는 364-451 ℃를 나타내었다. 가장 향상된 열팽창 계수(coefficient of thermal expansion, CTE)와 가스차단성은 TFB(3.23 ppm/℃)와 4,4-ODA(<10^(-2) cc/m2/day) 단량체를 각각 사용하였을 때 보였다. PI 필름의 투과도는 500 nm에서 65-89%를 보였으며, 노란색 정도를 나타내는 황색지수(yellow index, YI)는 3.01-69.52를 보였다.

Keywords: polyimide; hydroquinone bis(trimellitate anhydride); thermal property; optical transparency; gas permeation.

References
  • 1. Kinjo N, Numata S, Yokouama T, Plastics., 34, 81 (1983)
  •  
  • 2. Hasegawa M, Horie K, Prog. Polym. Sci., 26, 259 (2001)
  •  
  • 3. Yang F, Zhao J, Li Y, Zhang S, Shao Y, Shao H, Ma T, Gong C, Eur. Polym. J., 45, 2053 (2009)
  •  
  • 4. Jang W, Shin D, Choi S, Park S, Han H, Polymer, 48(7), 2130 (2007)
  •  
  • 5. Park JW, Lee M, Lee MH, Liu JW, Kim SD, Chang JY, Rhee SB, Macromolecules, 27(13), 3459 (1994)
  •  
  • 6. Ge Z, Fan L, Yang S, Eur. Polym. J., 44, 1252 (2008)
  •  
  • 7. Yin J, Ye YF, Li L, Zhang YL, Huang Y, Wang ZG, Eur. Polym. J., 35, 1367 (1999)
  •  
  • 8. Seo KS, Sul KI, Kim YS, Choi KY, Suh DH, Won JC, Polym.(Korea), 31(2), 130 (2007)
  •  
  • 9. Hasegawa M, Horiuchi M, Wada Y, High Perform. Polym., 19, 175 (2007)
  •  
  • 10. Liu JG, Zhao XJ, Fan HSL, Yang SY, High Perform. Polym., 18, 851 (2006)
  •  
  • 11. Maier G, Prog. Polym. Sci., 26, 3 (2001)
  •  
  • 12. Ando S, Matsuura T, Sasaki S, Polym. J., 29, 69 (1997)
  •  
  • 13. Yang CP, Su YY, Wu KL, J. Polym. Sci. A: Polym. Chem., 42(21), 5424 (2004)
  •  
  • 14. Ju CH, Kim JC, Chang JH, J. Appl. Polym. Sci., 106(6), 4192 (2007)
  •  
  • 15. Jin HS, Chang JH, Polym.(Korea), 32(3), 256 (2008)
  •  
  • 16. Min UK, Chang JH, Thick Films: Properties, Techmology and Applications, Nova Sci. Publishers Inc., N.Y., USA, Chapter 5 (2012)
  •  
  • 17. Choi IH, Chang JH, Polym. Adv. Technol., 22, 682 (2011)
  •  
  • 18. Liu JG, Nakamura Y, Shibasaki Y, Ando S, Ueda M, Macromolecules, 40(13), 4614 (2007)
  •  
  • 19. Oh MC, Zhang H, Szep A, Chuyanov V, Steier WH, Zhang C, Dalton LR, Erling H, Tsap B, Fetterman HR, Appl. Phys. Lett., 76, 3525 (2000)
  •  
  • 20. Ramiro J, Eguiazabal JI, Nazabal J, Eur. Polym. J., 42, 458 (2006)
  •  
  • 21. Vora RH, Mater. Sci. Eng. B., 168, 71 (2010)
  •  
  • 22. Hamciuc E, Hamciuc C, Cazacu M, Eur. Polym. J., 43, 4739 (2007)
  •  
  • 23. Yang CP, Su YY, Chen YC, Eur. Polym. J., 42, 721 (2006)
  •  
  • 24. Liaw DJ, Huang CC, Chen WH, Polymer, 47(7), 2337 (2006)
  •  
  • 25. Mehdipour-Ataei S, Hatami M, Eur. Polym. J., 41, 2010 (2005)
  •  
  • 26. Behniafar H, Banihashemi A, Eur. Polym. J., 40, 1409 (2004)
  •  
  • 27. Banihashemi A, Atabaki F, Eur. Polym. J., 38, 2119 (2002)
  •  
  • 28. Bruma M, Schulz B, Mercer FW, Polymer, 35(19), 4209 (1994)
  •  
  • 29. Lee C, Sundar S, Kwon J, Han H, J. Polym. Sci. A: Polym. Chem., 42(14), 3612 (2004)
  •  
  • 30. Jin HS, Chang JH, J. Appl. Polym. Sci., 107(1), 109 (2008)
  •  
  • 31. Domanska U, Zawadzki M, Krolikowski M, Lewandrowska A, Chem. Eng. J., 181, 63 (2012)
  •  
  • 32. Xue L, Desmarteau DD, Pennington WT, Solid State Sci., 7, 311 (2005)
  •  
  • 33. Domanska U, Paduszynski K, J. Chem. Thermodyn., 42(11), 1361 (2010)
  •  
  • 34. Kim SO, Jeon BH, Chung IJ, Polymer, 42(7), 3249 (2001)
  •  
  • 35. Hasegawa M, Kasamatsu K, Koseki K, Eur. Polym. J., 48, 483 (2012)
  •  
  • 36. Hasegawa M, Koseki K, High Perform. Polym., 18, 697 (2006)
  •  
  • 37. Hasegawa M, Sakamoto Y, Tanaka Y, Kobayashi Y, Eur.Polym. J., 46, 1510 (2010)
  •  
  • 38. Kim Y, Chang JH, Kim JC, Macromol. Res., 20(12), 1257 (2012)
  •  
  • 39. Choi CH, Kim YM, Chang JH, Polym. Sci. Technol., 23(3), 296 (2012)
  •  
  • 40. Choi IH, Chang JH, Polym.(Korea), 34(5), 480 (2010)
  •  
  • 41. Kim Y, Chang JH, Appl. Chem. Eng., 23(3), 266 (2012)
  •  
  • 42. Matsui S, Sato H, Nakagawa T, J. Membr. Sci., 141(1), 31 (1998)
  •  
  • 43. Min U, Kim JC, Chang JH, Polym. Eng. Sci., 51(11), 2143 (2011)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2013; 37(5): 618-624

    Published online Sep 25, 2013

  • Received on Apr 15, 2013
  • Accepted on Jun 25, 2013