  • Effect of Chemical Structure of Acrylate Monomer on the Transparent Acrylic Pressure Sensitive Adhesives for Optical Applications
  • Baek SS, Jang SJ, Lee SW, Hwang SH
  • 광학용 아크릴 점착제내 단량체 화학구조에 따른 점착특성
  • 백승석, 장세정, 이상원, 황석호
Abstract
To prepare transparent acrylic pressure sensitive adhesives (PSAs), terpolymer syrups were photopolymerized from 2-ethylhexyl acrylate and 2-hydroxyethyl acrylate with third monomer having different chemical structure. After polymerization, 1,6-hexanediol diacrylate as a crosslinker and a photoinitiator were added and then UV-irradiated to prepare the PSAs. The adhesion performances and optical characteristics of the PSAs were investigated. Their adhesion performance was dependent on the composition of monomers in the polymer chain but optical properties were maintained at a suitable level. The PSAs prepared by bulky and heteroatom-containing monomers such as IBOA, THFA, and ACMO showed better adhesion performance than others.

2-Ethylhexyl acrylate와 2-hydroxyethyl acrylate의 기본 구조에 다양한 곁사슬 화학구조를 가지는 단량체의 종류를 변화시키면서 광중합된 고투명 3원 공중합체 시럽을 합성하였다. 시럽에 가교제로 1,6-hexanediol diacrylate와 광개시제 를 혼합한 후 UV-광원을 조사시켜 점착제(PSAs)를 제조하여 점착특성과 광학특성을 고찰하였다. PSAs의 점착물성은 단량체 종류에 따른 조성비에 크게 의존하고 있으나, 광학적 특성이 유사함을 확인하였다. 상대적으로 부피가 큰 분자이면서 헤테로 원소를 포함하고 있는 IBOA, THFA, ACMO 단량체가 n-BA, VAc, CHA 단량체보다 좋은 점착물성을 보여주었다.

Keywords: pressure sensitive adhesive; photopolymerization; peel strength; tack; transmittance; acrylate monomer.

References
  • 1. Benedek I, Pressure Sensitive Adhesives and Application, 2nd Ed., Marcel Dekker, Inc., New York (2004)
  •  
  • 2. Creton C, Materials Science and Technology: A Comprehensive Treatment, VCH, Weinheim (1997)
  •  
  • 3. Shecut WH, Day HH, U.S. Patent 3,965 (1845)
  •  
  • 4. Levine IW, U.S. Patent 1,537 (1926)
  •  
  • 5. Baek SS, Jang SJ, Lee JH, Kho DH, Lee SH, Hwang SH, Polym.(Korea), 38(2), 199 (2014)
  •  
  • 6. Lee SJ, So JY, Park C, Ban TG, Park LS, J. Appl. Sci., 10, 1104 (2010)
  •  
  • 7. Lee SW, Park JW, Kwon YE, Kim S, Kim HJ, Kim EA, Woo HS, Swiderska J, Int. J. Adhes. Adhes., 38, 5 (2012)
  •  
  • 8. Czech Z, Wojciechowicz M, Eur. Polym. J., 42, 2153 (2006)
  •  
  • 9. Baek SS, Lee SW, Hwang SH, Polym.(Korea), 37(1), 121 (2013)
  •  
  • 10. Aubrey AW, Welding GN, Wong T, J. Appl. Chem., 10, 2193 (1969)
  •  
  • 11. Gronewaldt E, Coating, 5, 144 (1969)
  •  
  • 12. Piglowski J, Kozlowski M, Rheol. Acta, 24, 519 (1985)
  •  
  • 13. Chang MC, Mao CL, Vargas RR, U.S.Patent 4,564,664 (1986)
  •  
  • 14. Krampe SE, Moore CL, Taylor CW, U.S.Patent 4,732,808 (1988)
  •  
  • 15. Yi JZ, Goh SH, Polymer, 43(16), 4515 (2002)
  •  
  • 16. Bikermann JJ, Trans. Soc. Rheol., 2, 9 (1957)
  •  
  • 17. Leong YC, Lee LMS, Gan SN, J. Appl. Polym. Sci., 88, 2118 (1987)
  •  
  • 18. Sweet RP, Ulman KL, Proceed. Intern. Symp. Control. Rel. Bioact. Mater., 24, 621 (1997)
  •  
  • 19. Michaelis M, Brummer R, Leopold CS, Eur. J. Pharm. Biopharm., 86, 234 (2003)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2014; 38(5): 682-686

    Published online Sep 25, 2014

  • Received on Apr 20, 2014
  • Accepted on May 19, 2014