Article
  • Preparation and Physical Properties of Polypropylene/Cellulose Composites
  • Jang SY, Kim DS
  • 폴리프로필렌/셀룰로오스 복합재의 제조 및 물성
  • 장송이, 김대수
Abstract
Cellulose has attracted much attention as potential reinforcements in green composites. In this study, polypropylene (PP)/cellulose composites were prepared by melt-blending followed by compression molding. To improve interfacial bonding between PP and cellulose, maleic anhydride-grafted polypropylene (MAPP) was used. Mechanical properties of the PP/cellulose composites were investigated by UTM and izod impact tester. Thermal properties of the PP/cellulose composites were investigated by TGA and DSC. SEM images for the fracture surfaces of the composites showed that the MAPP was effective in improving PP/cellulose interfacial bonding. Tensile strength and modulus of the composite were maxima when MAPP content, based on cellulose content, was 3 wt%. With increasing cellulose content, the impact strength of the composites decreased but the tensile strength and modulus increased.

셀룰로오스는 그린 복합재의 보강재로서 많은 관심을 받고 있다. 본 연구에서는 용융혼합 및 압축성형에 의해 폴리프로필렌/셀룰로오스 복합재를 제조하였다. 폴리프로필렌과 셀룰로오스의 계면결합을 향상시키기 위해 말레산 무수물로 개질된 폴리프로필렌(MAPP)을 사용하였다. 폴리프로필렌/셀룰로오스 복합재의 기계적 특성을 알아보기 위해 만능재료시험기와 아이조드 충격시험기를 사용하였고 열적 특성을 조사하기 위해 TGA와 DSC를 사용하였다. 전자현미경(SEM)을 이용한 복합재의 파단면 관찰 결과 MAPP가 폴리프로필렌/셀룰로오스 계면결합 향상에 효과적인 것으로 나타났다. 셀룰로오스 함량 대비 MAPP의 함량이 3 wt%일 때 복합재의 인장강도와 인장탄성률이 최고치를 나타냈다. 셀룰로오스의 함량이 증가할수록 복합재의 충격강도는 감소하는 반면 인장강도와 인장탄성률은 증가하였다.

Keywords: polypropylene; cellulose; composite; maleic anhydride-grafted polypropylene; physical properties.

References
  • 1. An SH, Kim DS, Polymer(Korea), 38, 129 (2013)
  •  
  • 2. Bondeson D, Kvien I, Oksman K, ACS Symposium Series, 938, 10 (2006)
  •  
  • 3. Petersson L, Kvien I, Oksman K, Comp. Sci. Technol., 67, 2535 (2007)
  •  
  • 4. Panaitescu DM, Notingher PV, Ghiurea M, Ciuprina F, Paven H, Iorga M, Florea D, J. Optoelectron. Adv. Mater., 9, 2526 (2007)
  •  
  • 5. An SH, Kim DS, Polymer(Korea), 37, 204 (2012)
  •  
  • 6. Panaitescu DM, Donescu D, Bercu C, Vuluga DM, Iorga M, Ghiurea M, Polym. Eng. Sci., 47(8), 1228 (2007)
  •  
  • 7. Felix JM, Paul G, J. Appl. Polym. Sci., 42, 609 (1991)
  •  
  • 8. Qiu WL, Zhang FR, Endo T, Hirotsu T, J. Appl. Polym. Sci., 87(2), 337 (2003)
  •  
  • 9. Qiu WL, Endo T, Hirotsu T, J. Appl. Polym. Sci., 94(3), 1326 (2004)
  •  
  • 10. Hristov VN, Vasileva S, Krumova M, Lach R, Michler GH, Polym. Compos., 25, 521 (2004)
  •  
  • 11. Seo YW, Kim DS, Polym.(Korea), 38(3), 327 (2014)
  •  
  • 12. Joseph K, Thomas S, Pavithran C, Polymer, 37(23), 5139 (1996)
  •  
  • 13. Nachtigall SMB, Cerveira GS, Rosa SML, Polym. Test., 26, 619 (2007)
  •  
  • 14. Pracella M, Haque MM, Alvarez V, Macromol. Mater. Eng., 295, 949 (2010)
  •  
  • 15. Wang TY, Tsiang RCC, Liou JS, Wu J, Sheu HC, J. Appl. Polym. Sci., 79(10), 1838 (2001)
  •  
  • 16. Morgan S, Ye ZB, Subramanian R, Zhu SP, Polym. Eng. Sci., 50(5), 911 (2010)
  •  
  • 17. Nakatani H, Hashimoto K, Miyazaki K, Terano M, J. Appl. Polym. Sci., 113(3), 2022 (2009)
  •  
  • 18. Zhang W, He X, Li C, Zhang X, Lu C, Deng Y, Cellulose, 21, 485 (2014)
  •  
  • 19. Spoljaric S, Genovese A, Shanks RA, Compos. Part A-Appl. Sci. Manuf., 40, 791 (2009)
  •  
  • 20. Vanden Eynde S, Mathot V, Koch MHJ, Reynaers H, Polymer, 41(9), 3437 (2000)
  •  
  • 21. Kiziltas A, Gardner DJ, Han Y, Yang HS, Thermochim. Acta, 519(1-2), 38 (2011)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2015; 39(1): 130-135

    Published online Jan 25, 2015

  • Received on Jun 24, 2014
  • Accepted on Aug 6, 2014