Article
  • Synthesis and Properties of UV Curable Waterborne Polyurethane Acrylate Nanocomposite Films Based on the Surface Modification of γ-Al2O3
  • Ran W, Lin S, Rempel GL, Pan Q
  • UV 경화성 수분산 폴리우레탄 아크릴레이트에 표면개질된 γ-Al2O3가 함유된 나노복합재료 필름의 합성과 특성
Abstract
Waterborne polyurethane acrylate/surface-modified γ-Al2O3 (WPUA/SAl2O3) nanocomposite films were prepared via a UV-initiated free radical photopolymerization system composed of nanocomposite emulsion, reactive diluents and a photoinitiator. To improve the compatibility of inorganic and organic phases, γ-Al2O3 nanoparticles were surface-modified by γ-methacryloxypropyl trimethoxysilane and combined with a WPUA matrix. The WPUA oligomer was initially prepared by step-growth polymerization, and the content of hydrophilic chain extender, dimethylolpropionic acid (DMPA) was varied to investigate its effect on the properties of the oligomer emulsion. Performance of nanocomposite films with various loadings of SAl2O3 was evaluated by TGA and DSC, water uptake/swelling degree, surface wettability, tensile strength and elongation at break, etc. The results revealed that thermostability of the nanocomposite film was reinforced compared with the WPUA matrix. Swelling capacity and mechanical strength were also improved due to the increase of crosslinking density. Moreover, the optimum content of DMPA for oligomer synthesis was 5%.

Keywords: waterborne polyurethane acrylate; nanocomposite films; surface-modified γ-Al2O3; dimethylolpropionic acid

References
  • 1. Xu HP, Qiu FX, Wang YY, Wu WL, Yang DY, Guo Q, Prog. Org. Coat., 73, 47 (2013)
  •  
  • 2. Asif A, Shi WF, Shen XF, Nie KM, Polymer, 46(24), 11066 (2005)
  •  
  • 3. Li KB, Shen YD, Fei GQ, Wang HH, Li JY, Prog. Org. Coat., 78, 146 (2015)
  •  
  • 4. Yoon SH, Kim BK, Polym. Bull., 68(2), 529 (2012)
  •  
  • 5. Jeon JH, Park YG, Lee YH, Lee DJ, Kim HD, J. Appl. Polym. Sci., 132, 42168 (2012)
  •  
  • 6. Hwang HD, Park CH, Moon JI, Kim HJ, Masubuchi T, Prog. Org. Coat., 72, 663 (2011)
  •  
  • 7. Park JM, Lee YH, Park H, Kim HD, J. Appl. Polym. Sci., 131, 40603 (2014)
  •  
  • 8. Liu JC, Liu QH, Zheng XF, Liu R, Mu QD, Liu XY, Polym. Bull., 73(3), 647 (2016)
  •  
  • 9. Xu JH, Cai X, Shen FL, Appl. Surf. Sci., 379(-), 433 (2016)
  •  
  • 10. Cho YK, Lee WK, Polym. Korea, 40(3), 439 (2016)
  •  
  • 11. Kim SR, Park JY, Lee SG, Lee JD, Polym. Korea, 39(6), 902 (2015)
  •  
  • 12. Canak TC, Serhatli IE, Prog. Org. Coat., 76, 388 (2013)
  •  
  • 13. Park JM, Jeon JH, Lee YH, Lee DJ, Park H, Chun HH, Do Kim H, Polym. Bull., 72(8), 1921 (2015)
  •  
  • 14. Fang ZH, Duan HY, Zhang ZH, Wang J, Li DQ, Huang YX, Shang JJ, Liu ZY, Appl. Surf. Sci., 257(11), 4765 (2011)
  •  
  • 15. Fang ZH, Shang JJ, Huang YX, Wang J, Li DQ, Liu ZY, Express. Polym. Lett., 4, 704 (2010)
  •  
  • 16. Decker C, Masson F, Schwalm R, Polym. Degrad. Stabil., 83, 309 (2004)
  •  
  • 17. Wang X, Hu Y, Song L, Xing WY, Lu HD, Lv P, Jie, GX, J. Polym. Res., 18, 721 (2011)
  •  
  • 18. Kim HG, Min KE, Polym. Korea, 39(2), 256 (2015)
  •  
  • 19. Kim HG, Polym. Korea, 40(1), 9 (2016)
  •  
  • 20. Lin WC, Yang H, Wang TL, Shieh YT, Chen WJ, Express. Polym. Lett., 6, 2 (2012)
  •  
  • 21. Xu JW, Pang WM, Shi WF, Thin Solid Films, 514, 69 (2014)
  •  
  • 22. Nam DW, Nam BU, Cha BJ, Kim BJ, Polym. Korea, 31(2), 111 (2007)
  •  
  • 23. Seo B, Park S, Kim S, Ha KR, Polym. Korea, 40(3), 421 (2016)
  •  
  • 24. Zhang SW, Yu AX, Song XQ, Liu XY, Prog. Org. Coat., 76, 1032 (2013)
  •  
  • 25. Kim D, Jeon K, Lee Y, Seo J, Seo K, Han H, Khan S, Prog. Org. Coat., 74, 435 (2012)
  •  
  • 26. Mishra RS, Mishra AK, Raju KVSN, Eur. Polym. J., 45, 960 (2009)
  •  
  • 27. Nam KH, Seo K, Seo J, Khan SH, Han H, Prog. Org. Coat., 85, 22 (2015)
  •  
  • 28. Chen SL, Zhang SD, Li YF, Zhao GH, Rsc Adv., 5, 4355 (2015)
  •  
  • 29. Toker RD, Apohan NK, Kahraman MV, Prog. Org. Coat., 76, 1243 (2013)
  •  
  • 30. Wang X, Xing WY, Song L, Yu B, Hu Y, Yeoh GH, React. Funct. Polym., 73(6), 854 (2013)
  •  
  • 31. Ra SH, Lee HD, Kim YH, Polym. Korea, 39(4), 579 (2015)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 2017; 41(3): 385-393

    Published online May 25, 2017

  • 10.7317/pk.2017.41.3.385
  • Received on Aug 2, 2016
  • Accepted on Oct 23, 2016