A model was developed to express the diffusion coefficient of solutes through water swollen and semicrystalline polymeric networks. This model is based on extension of Peppas - Reinhart''s model with the crystallites described as impermeable diffusion barriers forming the "walls" of hypothetical amorphous pores. The generalized diffusion model for the semicrystalline water swollen PVA membranes is proposed as the following equation : D_c/D_2,1=[(1-v_c)/r]f[(M_c-M_c^*)/(M_n-M_c^*)]exp[-πr_s²l_sv₃/V₁v₁] It has been shown that the normalized diffusion coefficients decrease linearly as the equilibrium volume fractions of crystalline membranes increase. This model was applied to the permeation experiments of theophylline and vitamin B)? through semicrystalline PVA membranes. These membranes were prepared by that treatment (annealing) of amorphous PVA membranes. The degree of crystallinity varies between 21.1% and 40.5% on a dry basis. The size of the crystallites was 48.3A and the interplanar spacing of (101) crystallographic plane was 4.56A.

팽윤된 준결정성 poly(vinyl alcohol)가교막을 통한 용질의 확산에 결정화도가 미치는 영향을 설명할 수 있는 새로운 모델을 개발하였다. 무정형 팽윤 가교막을 통한 용질의 확산 모델인 Poppas-Reinhart모델을 변형, 결정화도와 normal 용질 확산계수의 정량적인 관계를 다음 식으로 나타내었다. D_c/D_2,1=[(1-v_c)/r]f[(M_c-M_c^*)/(M_n-M_c^*)]exp[-πr_s²l_sv₃/V₁v₁]Glutaraldehyde로 가교한 PVA 막을 90-120℃에서 열처리 하여 결정성을 부여하였으며 theophilline과 vitamin B₁₂를 용질로 선택하여 확간 실험을 하였다. 그 결과 결정의 평형 부피분율의 감소에 따라 normal 용질 확산계수가 비례적으로 감소함을 확인하여 이 모델을 적용할 수 있음을 입증하였다.. 제조한 막의 결정화도는 21.1%에서 40.5%사이의 값을 얻었고 결정 크기는 48.3A인 것이 내부 평면 간격 4.56A으로 되어 있었다.