Porous poly(chloromethyl styrene) (PCMS) resins were synthesized by suspension polymerization. The cationic resins having quaternary ammonium groups were prepared by the reaction of the synthesized resins with tertiary amines. The effects of the content of the crosslinking agent and diluent on the structure and characteristics of the resins were investigated. It was found that density, water content, and ion-exchange capacity of resins were increased with the decrease of crosslinking agent and with the increase of diluent content. whereas the fixed charge density was decreased. The reactivity of resins with amines increased with the decrease of length of the alkyl chains, and then ion-exchange capacity increased as well. The sorption behaviour of the cationic resins was also investigated by using the sodium salt.

분산중합법에 의하여 다공성구조를 갖는 Poly(chloromethyl styrene) (PCMS) 수지를 합성하고 3차 아민과 반응시켜 4차 암모늄기가 고정된 양이온 수지를 제조하였다. 기질수지 합성시 가교제 및 기공형성제(diluent)의 함량을 변화시켰으며, 양이온 수지의 제조시 알킬기의 길이가 다른 3차 아민을 사용, 이들 변수가 수지의 구조 및 특성에 미치는 영향을 조사하였다. 가교제의 함량이 적고, 기공형성제(diluent)의 함량이 많을수록 수지의 밀도, 함수율, 이온교환용량 등은 큰 값을 보였으며, 고정하전밀도는 감소하였다. 또한 알킬기의 길이가 짧을수록 기질수지와 아민과의 반응성은 높아짐을 알 수 있었으며, 이에 따라 이온교환용량 역시 증가함을 보였다. 나트륨염을 사용하여 양이온 수지의 수착거동에 관하여서도 조사하였다.