  • Preparation and Properties of Nylin-Polypyrrole Conductive Composite Films Prepared by Gas State Polymerization
  • Im SS, Kang EY, Byun SW
  • 기상 중합법에 의한 Nylon 6-Polypyrrole Conductive Composite Film의 제조와 성질
  • 임승순, 강은영, 변성원
Abstract
Highly conducting Nylon 6-Polypyrrole composites can be chemically obtained by exposing Nylon 6 films containing FeC13 to vapour of pyrrole. The surface and bulk conductivities of these composites were in the range of 10-12-10-3S/ cm depending on the concentration of FeCl3 and the polymerization time. From the current-voltage characteristics and temperature dependence of conductivities, we can conclude that the conduction mechanism of Nylon 6-Polypyrrole composites mainly depends on electronic conduction. These composite films were analysed by FT-IR spectroscopy and wide angle X-ray scattering(WAXS). From the WAXS study, there are no appreciable changes of the crystal structure of Nylon 6 composite films, but the formation of α-type crystal of Nylon 6 is suppressed during the polymerization of pyrrole. The dynamic and static mechanical properties were studied with Rheovibron and Instron, respectively. These composite films exhibited good mechanical properties.

FeCl3를 함유하는 Nylon 6 film을 pyrrole monomer의 증기에 노출시켜 높은 전기전도성을 갖는 Nylon 6-Polypyrrole composite를 화학적으로 제조하였다. 이 복합재료의 표면과 체적전도도는 FeCl3의 농도와 중합시간에 따라 10-12-10-3S/ cm의 범위를 나타내었다. 전류-전압특성과 전기전도도의 온도의존 성실험으로 부터 Nylon 6-Polypyrrole composites의 전도 mechanism은 주로 electronic conduction mechanism을 나타내었다. 이 composite film에 대하여 FT-IR spectrum분석과 광각 X-ray 산란 (wide angle X-ray scattering) 실험을 행하였으며, 광각 X-ray산란 실험으로 부터 이 복합재료의 결정구조는 큰 변화는 없었으나, pyrrole이 중합됨에 따라 Nylon 6의 α-type 결성의 형성이 억제되었다. 동력학적 성질 및 기계적 성질을 Rheovibron과 Instron으로 조사하였으며, 그 결과 이복합재료의 물성은 상당히 우수 하였다.

References
  • 1. Kaneto K, Yoshino K, Inuishi Y, Jpn. J. Appl. Phys., 21, L567 (1982)
  •  
  • 2. Ohsawa T, Kaneto K, Yoshino K, Jpn. J. Appl. Phys., 23, L527 (1984)
  •  
  • 3. Yoshino K, Kaneto K, Inoue S, Tsukagoshi K, Jpn. J. Appl. Phys., 22, L701 (1983)
  •  
  • 4. Bjorklund R, Lundstrom I, J. Electron. Mat., 13, 211 (1984)
  •  
  • 5. Audebert P, Bidan G, Synth. Met., 14, 71 (1986)
  •  
  • 6. Ojio T, Miyata S, Polym. J., 18, 95 (1986)
  •  
  • 7. Sugimoto R, Gu HB, Hayashi S, Yoshino K, Synth. Met., 18, 247 (1987)
  •  
  • 8. Pron A, Kucharski Z, Budrowski C, Agorskaa MZ, Krichene S, Suwalski J, Dehe G, Lefrant S, J. Chem. Phys., 83, 5923 (1985)
  •  
  • 9. Nakanishi K, Solomon PNInfrared Absorption Spectroscopy, Holden-Day, San Francisco (1977)
  •  
  • 10. Pron A, Zagorska M, Fabianowski W, Polym. Commun., 28, 19 (1987)
  •  
  • 11. Parker JP, Lindenmeyer PH, J. Phys. Sci., 21, 821 (1977)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1990; 14(1): 62-69

    Published online Feb 25, 1990