  • Synthesis and Properties of Polyesters Containing Spiroacetal Unit
  • Rhee JM, Lee KS, Choi KY
  • 스피로아세탈을 포함하는 폴리에스테르의 합성 및 물성
  • 이종문, 이광섭, 최길영
Abstract
Several polyspiroacetals were synthesized by interfacial polyconcensation from 3, 9-bis(4-hydorxyphenyl)-2, 4, 8, 10-tetraoxaspiroundecane [SAB] with aliphatic acid chloride. The majority of these polymer were soluble in polar solvents like m-cresol and phenol/tetrachloroethane(1 : 1), and the inherent viscosities were ranged from 0.15 to 0.29dl/g. The Tg''s were detectable at 60∼125℃, whose values decreased with increasing aliphatic chain length. 5% Weight loss in TG curve were detected at 305∼333℃ in N2 gas atmosphere. X-ray diffractograms showed that all of the polymer are crystalline at room temperature.

여러종류의 폴리스피로아세탈은 3,9-bis(4-hydroxypheny)-2, 4, 8, 10-tetraoxaspiroundecane[SAB]과 지방족 산염화물의 계면축중합반응에 의해 합성되었다. 이들 중합체의 대부분은 m-크레졸과 페놀/테트라크로로메탄(1 : 1)등과 같은 극성용매에 용해되었으며 용액점성도(ηinh)는 0.15∼0.29dl/g이었다. DSC에 의한 열분석결과 Tg는 60∼125℃에서 측정되었는데 이들은 중합체의 유연성 사슬길이가 증가할 수록 감소하는 경향을 나타냈다. TG 분석에 의하면 5% 무게감량이 305∼333℃ 범위에서 관찰되어 일반적인 아세탈 중합체보다 열안정성이 양호함을 알수 있었다. X-선 회절실험에서 중합체들이 상온에서 결정성임이 확인되었다.

References
  • 1. Read J, J. Chem. Soc., 101, 2090 (1912)
  •  
  • 2. Fairbourne A, Woodley JW, J. Chem. Soc., 130, 3240 (1926)
  •  
  • 3. Mkhitaryan VG, J. Gen. Chem., 9, 1923 (1939)
  •  
  • 4. Abbott LS, Faulkner D, Hollis CEU.S. Patent, 2,739,972 (1956)
  •  
  • 5. Conrad WE, Gesner BD, Levasseur LA, Murphy RF, Conrad HM, J. Org. Chem., 26, 3571 (1961)
  •  
  • 6. Orth H, Kunststoffe, 41, 454 (1951)
  •  
  • 7. Kress BHU.S. Patent, 2,785,996 (1957)
  •  
  • 8. Cohen SM, Lavin E, J. Appl. Polym. Sci., 6, 508 (1962)
  •  
  • 9. Bailey WJ, Volpe AA, Polym. Prepr., 8, 92 (1967)
  •  
  • 10. Kurita K, Hirakawa N, Dobashi T, Iwakura Y, J. Polym. Sci. A: Polym. Chem., 17, 2567 (1979)
  •  
  • 11. Akar A, Talinli N, Makromol. Chem. Rapid Commun., 10, 127 (1989)
  •  
  • 12. Komminoth P, Poppenwimmer K, Redel H, Robinson TGer, Offen. 2,151,724 (1972)
  •  
  • 13. Miyamoto A, Matsukawa HGer. Offen., 2,343,800 (1974)
  •  
  • 14. Matsukawa H, Saeki KGer. Offen. 2,404,412 (1974)
  •  
  • 15. Yukuta T, Oobashi T, Yoshii HJapan Kokal 75,91,462 (1975)
  •  
  • 16. Magosch JH, Karl H, Rueter JGer. Offen. 2,448,954 (1976)
  •  
  • 17. Heller J, Penhale DWH, Panburn SH, Prog. Biomed. Eng., 5, 175 (1988)
  •  
  • 18. Hirose S, Hatakeyama T, Hatakeyama H, Sen-I Gakkaishi, 38, 507 (1982)
  •  
  • 19. Lee KS, Won JC, Jung JC, Makromol. Chem., 190, 1547 (1989)
  •  
  • 20. Ballauff M, Makromol. Chem. Rapid Commun., 7, 407 (1986)
  •  
  • 21. Fletcher SE, Mortimer CT, Springall HD, J. Chem. Soc., 81, 580 (1959)
  •  
  • 22. Ballauff M, Schmidt GG, Mol. Cryst. Liq. Cryst., 147, 163 (1987)
  •  
  • 23. Lee KS, Lee BW, Jung JC, Lee SM, Polym.(Korea), 13(1), 47 (1989)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1990; 14(5): 448-455

    Published online Oct 25, 1990