Article
  • Synthesis and Properties of polycarbonate-type Polyurethane
  • Park SH, Lee SH, Noh ST, Kim KY
  • Polycarbonate형 Polyurethane의 합성과 물성
  • 박순호, 이순홍, 노시태, 김계용
Abstract
Three kinds of polycarbonate glycols were synthesized from the condensation reation of 1,6-hexanediol, 1,4-buthanediol and neopentylglycol with diethycarbonate respectively. And polycarbonate-type polyurethanes were obtained with further reation of these glycols and MDI, and 1,4-buthanediol. Mechanical, thermal properties, water proofness and gas permeability were measured. Glass transition temperature of polyurethane having hexamethylene, tetramethylene group in the main chain appeared near -30℃, -20℃ respectively. However neopentyl type polyurethane has much high Tg around 30-40℃. The mechanical properties of polyurethane increased, but the relative crystallinities decreased with the increasing the amp)tint of chain extender. From the gas permeability test, polycarbonate-type polyurethane membranes having tetramethylene and neopenthyl group showed higher permeability coefficient and higher O2-selectivity than the polyether or polyester type polyurethane.

1.6-hexanediol, 1,4-butanediol 및 neopentyl glycol을 diethylcarbonate와 각각 축합 반응을 시켜 polycarbonate glycol을 합성하고, 이를 methylenediphenyldiisocyanate(MDI). 1,4-butanediol과 반응시켜 3종의 폴리카보네이트형 우레탄 수지를 합성하였다. 제조한 우레탄 수지의 기계적 성질. 열적 성질 및 내가수분해성 등을 측정하고. 고분자 막 소재로서의 특성을 검토하기 위하여 산소와 질소에 대한 투과실험을 행하였다. 합성한 폴리카보네이트형 우레탄수지 중 hexamethylene계 우레탄 수지는 유리전이온도(Tg)가 -30근 부근의 유연하면서 강인한 필름이 얻어졌으며. tetrame-thyene계 우레탄 수지의 Tg는 -20℃ 부근의 값을 나타냈으나, neopentyl계 우레탄 수지는 Tg가 30∼40℃로 부근의 값을 나타내었다. 쇄연장제의 양을 증가시킴에 따라 기계적 물성은 향상되었으나 상대적 결정화도는 감소되었다. 내가수분해성은 3종 모두 polyether형 우레탄 수지보다 15∼20%가량 우수함을 알 수 있었다. 한편 기체투과 식험 결과 hexamethyle계와 neopentyl계 우레탄 수지는 기존의 우레탄 막 보다 높은 투과계수를 나타냈으며 질소에 대한 산소의 선택성이 크고 온도증가에 따라 투과율이 증가됨을 알 수 있었다.

References
  • 1. Schneider NS, J. Macromol. Sci.-Phys., 5, 23 (1969)
  •  
  • 2. Brauman SK, J. Appl. Polym. Sci., 16, 243 (1972)
  •  
  • 3. Reid JC, Eur. Polym. J., 5, 565 (1969)
  •  
  • 4. Mori Y, Tanzawa H, Kobunshi, 22, 613 (1973)
  •  
  • 5. Kim JH, Kim KY, Polym.(Korea), 10(6), 620 (1986)
  •  
  • 6. Kim JH, Kim KY, Polym.(Korea), 8(2), 98 (1984)
  •  
  • 7. Brash JL, Fritziager BK, J. Biomed. Mater. Res., 7, 313 (1973)
  •  
  • 8. Rattnner BD, Hoflman AS, ACS Symp. Ser., 31, 1 (1976)
  •  
  • 9. Min DS, Lee KH, Kim KY, Polym.(Korea), 7(2), 96 (1983)
  •  
  • 10. Kim KY, Lee KH, Shim BS, Polym.(Korea), 5(5), 362 (1981)
  •  
  • 11. Dieterich K, Keberle W, Wues R, J. Oil Col. Chem. Assoc., 53, 363 (1970)
  •  
  • 12. Mctsuda K, Ohmura H, Tanaka Y, Sakai T, J. Appl. Polym. Sci., 23, 141 (1979)
  •  
  • 13. Dieterich D, Keberle W, Witt H, Angew. Chem.-Int. Edit., 9, 40 (1970)
  •  
  • 14. Kumarand CS, Rajadurai S, Leather Sci., 32, 231 (1985)
  •  
  • 15. Carothers WH, VanNatta FJ, J. Am. Chem. Soc., 52, 314 (1930)
  •  
  • 16. Sarel S, Pohoryles LA, J. Am. Chem. Soc., 80, 4596 (1958)
  •  
  • 17. Hill JW, Carothers WH, J. Am. Chem. Soc., 55, 5031 (1933)
  •  
  • 18. Harris RF, J. Appl. Polym. Sci., 37, 183 (1989)
  •  
  • 19. Park DW, Lee YK, Kim SC, Polym.(Korea), 6(2), 127 (1982)
  •  
  • 20. Minoura N, Kakagana T, J. Appl. Polym. Sci., 23, 815 (1979)
  •  
  • Polymer(Korea) 폴리머
  • Frequency : Bimonthly(odd)
    ISSN 0379-153X(Print)
    ISSN 2234-8077(Online)
    Abbr. Polym. Korea
  • 2022 Impact Factor : 0.4
  • Indexed in SCIE

This Article

  • 1990; 14(5): 487-496

    Published online Oct 25, 1990