Recycled high impact polystyrene powder and rice husk flour (RHF) were melt mixed with a twin-screw extruder or blended in a mixer, then injection molded to measure the mechanical properties. Four RHF contents (5, 10, 15, and 20 wt%) were used for melt mixing, and three RHF contents (10, 15, and 20 wt%) were used for direct injection. The heat resistance of the composite was enhanced above 485 ℃ due to the decomposition residue of RHF. The tensile and flexural strengths of the composite manufactured by melt mixing showed maximum values at 5 wt% RHF content, and the tensile and flexural moduli increased in proportion to the RHF content. In addition, as the RHF content increased, the notched Izod impact strength decreased, but the density increased. Dispersed RHF particles were shown in the scanning electron microscopy (SEM) images. For directly injected composites, mechanical properties, excluding elastic modulus, were lower than those of melt-blended composites. This study demonstrated that recycled high-impact polystyrene powder and RHF can be used to produce environmentally friendly and cost-effective products.

재활용 고충격폴리스티렌 분말과 왕겨분말을 이축압출기로 용융 훈련하거나 분말끼리 혼합한 후 사출하여 기계적 물성을 측정하였다. 용융혼련 후 사출한 경우는 4가지의 왕겨분말 함량(5, 10, 15 및 20 wt%)이 사용되었고 단순 혼합 후 사출한 경우는 3가지의 왕겨분말 함량(10, 15 및 20 wt%)이 사용되었다. 복합재료의 내열성은 왕겨분말의 분해 잔류물로 인해 485 ℃ 이상에서는 향상되었다. 용융혼련으로 제조한 복합재료의 인장 및 굴곡강도는 왕겨분말 5 wt%에서 최대값을 보였고 인장 및 굴곡탄성률은 왕겨분말 함량에 비례하여 증가하였다. 그리고, 왕겨분말 함량 증가 시 노치드 Izod 충격강도는 감소하였으나 밀도는 증가하였다. 분산된 왕겨분말들은 scanning electron microscopy (SEM) 이미지에서 확인할 수 있었다. 직접 사출한 복합재료의 경우 탄성률을 제외한 기계적 물성이 용융혼련한 경우보다 낮게 나타났다. 재활용 고충격폴리스티렌 분말과 왕겨분말을 사용하여 친환경적이면서 경제적인 제품을 생산할 수 있음을 확인하였다.

Keywords: recycled high impact polystyrene, rice husk flour, thermal properties, mechanical properties, morphology.