This paper deals with the synthesis of poly(propargyl trimethylammonium tetraphenylborate) having a highly bulky substituent, methylene trimethylammonium tetraphenylborate on the acetylene carbon, and its characterization. The polymerizations of propargyl trimethylammonium tetraphenylborate using transition metal catalysts including PdC1₂, PtCl, RuC1₃, etc. were proceeded well to give a relatively high yields of polymer (67-99%). The resulting polymers were mostly insoluble in common organic solvents, and separated as a brown and black solids. Instrumental analyses on the polymer structure suggested that the resulting polymer had a conjugated polymer backbone with the methylene trimethylammonium tetraphenylborate substituent. X-ray diffraction analysis revealed that the polymer is amorphous.

본 논문은 큰 치환기인 메틸렌 트리메틸암모늄 테트라페닐보레이트를 치환기로 갖는 공액구조 고분자인 폴리(프로파길 트리메틸암모늄 테트라페닐보레이트)의 합겅과 그 특성조사에 관한 연구내용을 다룬 것이다. PdCl₂2 PtCl₂, RuCl₃ 등의 전이금속 촉매를 사용해서 중합시켰을 경우 중합반응이 잘 진행되었으며 비교적 높은 수율(67-99%)의 중합체를 얻을 수 있었다. 합성한 중합체는 그 합성방법에 관계없이 유기용매에 대부분 용해하지 않았으며 갈색 혹은 검은색의 분말상이었다.본 중합체 구조에 대한 기기분석 결과 이 고분자는 치환기로 메틸렌 트리메틸암모늄 테트라페닐보레이트를 갖는 공액구조 고분자임을 확인할 수 있었바. X-선 회절분석 결과 본 중합체는 대부분 무정형임을 알 수 있었다.

Keywords: conjugated polymer; polyelectrolyte; transition metal catalyst; morphology