We studied the preparation and property of second-order nonlinear optical(NLO) material with polyimide containing hexafluoroisopropylidene unit and Disperse red 1. Polyamic acid, silylated Disperse red 1, and silane coupling agent were mixed to prepare the solution through hydrolysis and condensation. Thin film was fabricated using the prepared solution and imidized after poling. Before imidization, we could observe the enhancement of poling efficiency under the excitation light in polyamic acid form. The electro-optic coefficient γ₃₃ was determined to be 33.2 pm/V at 632 nm, and was observd to be stable at 100 ℃. The organic/inorganic composite NLO material showed good temporal stability at high temperature arising from the imidization and increase of the density of Si-O-Si bond.

Hexafluoroisopropylidene을 포함하는 폴리이디와 Disperse red 1을 사용하여 이차비선형 광학재료의 제조와 특성에 관하여 연구하였다. Disperse red 1을 포함하는 알콕시 실란과 불소계 polyamic acid 혼합용액에 실란계 가교제를 도입하고, 가수분해 및 축합반응 후 필름을 형성하고 이을 분극처리 후, 이미드와 반응을 진행시켰다. 이미드화 전의 polyamic acid 상태에서 광에 의해 분극효과가 상승하는 현상을 관찰할 수 있었다. 전기광학계수인 γ₃₃의 값은 632 nm에서 33.2 pm/V를 나타내며 100 ℃에서 열적으로 안정함을 관찰할 수 있었다. 유기/무기 복합형태의 비선형 공학재료는 이미드 결합이 형성됨에 따른 효과와 Si-O-Si 결합밀도의 증가에 의해 전기광학 특성의 고온에서의 우수한 경시안정성을 관찰할 수 있었다.

Keywords: polymide; sol-gel process; nonlinear optical material; disperse red 1; electro-optic coefficient