When polyethylene terephthalate(PET) film specimen were stepwise elongated under tension with various speeds of about 0.5~500 mm/min, the necking area, consisted of transparent and opaque bands, was formed during plastic deformaiton. Stress oscillation was apparently obtained in the stress-strain curve of above specimen. However, stress oscillation was not obtained in the stress-strain curve of annealing specimen. Microstructure was examined dynamically using an optical microscopy and thermal analysis was carried out in a differential scanning calorimeter at a heating rate of 10 ℃/min. Also, orientation and crystallization were exmined using monochromatic-pinhole technique and elastic modulus was measured by a dynamic mechanical analyzer in the temperature range of -150~70 ℃ with the frequency of 1 Hz. Transparent PET products were fabricated by use of the PET pellets annealed at 83 ℃ for 30 min in an electric furnace.

Polyethylene terephthalate(PET) 필름 시편을 약 0.5~500 mm/min의 속도까지 단계적으로 연신시켰을 때, 플라스틱 변형이 일어나는 동안에 투명 및 불투명 밴드들이 존재하는 넥킹영역이 형성되었다. 상기 시편의 응력-변형 곡선을 살펴보면, 응력 진동이 뚜렷하게 발생하였음을 확인할 수 있었다. 한편, 열처리된 시편의 응력-변형 곡선을 살펴보면, 응력 진동이 발생하지 않았음을 확인할 수 있었다. 시편들의 미세구조는 광학 현미경을 통하여 동적으로 관찰하였고, 시편들의 열적 특성은 시차 주사 열량기를 사용하여 10 ℃/min의 승온 속도에서 측정하였다. 또한, 시편들의 배향화 및 결정화 정도는 단색-핀홀법을 이용하여 측정하였고, 시편들의 탄성계수는 동적 기계 분석기를 통하여 -150~70 ℃의 온도 범위에서 1 Hz의 주파수 대에서 측정하였다. PET 펠렛을 전기로에서 약 83 ℃에서 30분 동안 열처리하여 투명한 PET 제품을 제작하였다.

Keywords: PET; opaque; transparent; deformation; stress; oscillation; annealing